ERCuAl-A2鋁青銅焊絲 HSCuA2銅焊絲HS214

牌 號	主要成份(%)	特性和用途	相當AWS
黃銅焊絲 GMT-CU	Sn Cu Rem	機械性能好，耐磨性好，流動性非常優秀，適合無溫冷焊。	ERCuSn-D
紫磷銅焊絲S201	P0.5 Cu Rem.	機械性能好，抗裂性好。紫銅氣焊及氬弧焊用	ERCu
硅青銅焊絲S211	Si3 Mn1 Cu Rem.	機械性能好，銅合金氬弧焊及鋼的MIG釬焊用	ERCuSi-Al
錫青銅焊絲S212	Sn5 Cu Rem.	耐磨性好。銅合金氬弧焊及鋼的堆焊用	ERCuSn-A
錫青銅焊絲S213	Sn8 Cu Rem.	耐磨性好。銅合金氬弧焊及鋼的堆焊用	ERCuSn-C
鋁青銅焊絲A1S214	Al7.5 Cu Rem.	耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用	ERCuAl-A1
鋁青銅焊絲A2S215	Al9 Cu Rem.	耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用	ERCuAl-A2
鋁青銅焊絲(A3)	A1 10.5 Cu Rem.	耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用。	ERCuA1-A3
錫黃銅焊絲S221	Cu60 Sn1 Si0.3 Zn Rem.	熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
鐵黃銅焊絲S222	Cu58 Sn0.9 Si0.1 Fe0.8 Zn Rem.	熔點約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵	RBCuZn-C
鎳鋁青銅焊絲-1	Al8 Ni2 Cu Rem	熔點約1038℃-1054℃。耐磨耐蝕，銅合金氬弧焊及鋼的釬焊。
鎳鋁青銅焊絲-2	Al8 Ni6 Cu Rem	熔點約1038℃-1054℃。耐磨耐蝕，銅合金氬弧焊及鋼的釬焊。	ERCuNiAl
鋅白銅焊絲S225	Cu48 Ni10 Zn Rem.	熔點約935℃。高強度,釬焊鋼、鎳及硬質合金用	RBCuZn-D2
S225F	Cu48 Ni10 Zn Rem.	外涂焊劑的S225焊絲	RBCuZn-D
S226	Cu60 Sn0.3 Si0.2 Zn Rem.	熔點約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵
S227	Cu58 Sn0.9 Ni0.5 Si0.1 Fe0.8 Zn Rem.	熔點880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵	RBCuZn-B
S229	Cu55 Ni6 Mn4 Zn余量	熔點約920℃。高強度,釬焊鋼、鎳及硬質合金用

HB-YD601(Z)	3～5	1.4～1.6	0.6～1.0	28～30	?0?2	?0?2	?0?2	HRC ：59～61	用于磨煤輥、磨盤的修復和再制造，以及輸送帶、料斗、挖掘機、鏟齒、筑路機、采石場設備、混料機和鼓風機葉片等堆焊。
HB-YD605(Z)	3～5	1.4～1.6	0.6～1.0	28～30	?0?2	?0?2	B：1～2	HRC ：63～65	用于磨煤輥、磨盤的修復和再制造，以及輸送帶、料斗、挖掘機、鏟齒、筑路機、采石場設備、混料機和鼓風機葉片等堆焊。
HB-YD611(M)	3～5	1.4～1.6	0.6～1.0	28～30	?0?2	?0?2	?0?2	HRC ：59～61	用于磨煤輥、磨盤的修復和再制造，以及輸送帶、料斗、挖掘機、鏟齒、筑路機、采石場設備、混料機和鼓風機葉片等堆焊

HB-YD467耐磨藥芯焊絲

說明： YD132-1是CO2氣體保護的CrMo型堆焊藥芯焊絲。堆焊時電弧穩定，脫渣容易。
用途：適用于耐沖擊，中度磨損的情況。用于低碳鋼、中碳鋼或低合金鋼機件表面的修補，如礦山、農業機械的堆焊與修補。
熔敷金屬化學成分（％）（保護氣體:CO2）
項目 C Cr Mo
保證值 ≤0.50 ≤3.00 ≤1.50
堆焊層硬度：HRC≥30
參考電流（DC+）
焊絲規格（mm） 焊接電流（A） 焊接電壓（V）
φ1.2
φ1.4
φ1.6 220 26
注意事項:
1.施焊工件應做除油、除銹處理。
2.焊接時，氣體流量一般在20～25L/min。
3.藥芯焊絲焊接時，干伸長度應為15～25mm。
4.在堆焊大型工件前應適當預熱至300℃左右。
5.焊絲庫房的濕度應保持在小于60% 。
6.非真空包裝焊絲存放時間不宜超過半年，真空包裝焊絲存放時間不宜超過一年。

YD798耐磨焊絲YD798藥芯焊絲詳細介紹：

氣體保護焊堆焊焊絲Gas ShieldedHardfacing Wires

牌號
Trade Name
直徑
Diameter
HRC
（國家標準臺式硬度計）
特點及主要用途
characteristicsandapplication
HB-YD114(Q)
1.6
50-55
(受強烈沖擊后
After high impact)
高錳鋼堆焊焊絲，受強烈沖擊后，表面具有加工硬度的特點。
High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
HB-YD115(Q)
1.6
50-55
(受強烈沖擊后After high impact)
用于受嚴重沖擊高錳鋼堆焊，加工硬化效果顯著。
Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
HB-YD165(Q)
1.6
60-65
高硬度耐磨焊絲，適用于磨粒磨損表面堆焊
High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
HB-YD172(Q)
1.6
≥40
用于堆焊齒輪、挖泥斗、礦山機械等磨損件
Applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery.
HB-YD207(Q)
1.6
≥50
用于堆焊推土機刀片，螺旋槳等磨損零件
Applied to repair surface of high wear parts, such as bulldozer blade and propeller.
HB-YD212(Q)
1.2/1.6
≥50
用于堆焊各種受磨損的機件表面，如齒輪、挖斗、礦山機械
Applied to repair surface of wear parts, such as gear mud bucket and mining machinery.
HB-YD256(Q)
1.6
HB≥170
高錳鋼堆焊，適用于破碎機等受沖擊磨損部位的堆焊
High-manganese steelhardfacing flux-cored Wires,it is applied to repair surface of high impact wear parts, such as Crusher.
HB-YD258(Q)
1.6
55-60
用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-YD265(Q)
1.6
60-65
高硬度耐磨焊絲，適用于磨粒磨損表面堆焊
High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
HB-YD322(Q)
1.6
≥55
用于堆焊各種沖模及切削刃具，兼用于修復要求耐磨損性能較高之機械零件
Applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery.
HB-YD327A(Q)
1.6
≥55
專門用于模具堆焊，耐磨性能高于D322
Used tomouldsurfacing, wear resistance is better than D322.
HB-YD337(Q)
1.6
≥48
用于鑄鋼或鍛鋼上堆焊鍛模
Applied to repairfo r g ing dieatcast steelorfo r g ing steel.
HB-YD397(Q)
1.6
≥40
用于堆焊鑄鋼或鍛鋼做坯體的熱鍛模或堆焊高強度耐磨件
Applied to repair hotfo r g ing dieatcast steelor fo r g ing steel, or highstrengthwear surfacing.
HB-YD405A(Q)
1.6
50-59
用于熱軋輥開坯輥堆焊
Applied to repair hot-rolling blooming rollor.
HB-YD430A(Q)
1.6
20-35
打底層堆焊焊絲
A backing hardfacing flux-cored Wires
HB-YD488A(Q)
1.6
45-50
用于軋輥堆焊
Applied to repair rollor
HB-YD507Mo(Q)
1.6
35-45
用于510℃以下中高壓閥門堆焊
Applied to valve which operating temperature is less than 510℃.
HB-YD518(Q)
1.6
40-50
用于連鑄輥堆焊
Applied to repaircontinuous caster roller
HB-YD688(Q)
1.6
50-60
用于磨煤輥打底焊(韌性好，可以多層堆焊)
Used to coal roller backing welding.
HB-YD788(Q)
1.6
55-62
硬度高，可以多層堆焊。
High hardness andmulti-layer welding
HB-YD888(Q)
1.2, 1.6
60-65
硬度高，堆焊層厚度不超過6mm。
High hardness, but thethicknessofsurfacing layeris less than 6mm.
HB-YD888Ni(Q)
1.2
58-65
高鉻合金焊絲，用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-YD988(Q)
1.6
55-63
高鉻合金焊絲，用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-YD990(Q)
1.6
55-65
用于高溫耐磨堆焊。
Applied to repair surface ofhigh temperaturewear parts.
HB-YD58(Q)
1.6
55-60
高溫耐磨焊絲，用于化推焦機磨靴的堆焊。
high temperaturewear hardfacing wires,
HB-YD67(Q)
1.6
58-63
用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-YD95(Q)
1.6
55-63
高鉻合金焊絲，用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-DG7(Q)
1.6
52-60
地鐵盾構施工刀具刃口堆焊專用，也可用于煤碳石裝載機料斗和刃口堆焊修復。
Applied to repair surface of high impact wear parts, such as shiled machine, excavator bucket and hopper of mining machinery products.