不同鉻鉬鋼焊接接頭的熱處理規(guī)范
|
|
碳
鋼 |
C-Mo |
1/2Cr-1/2Mo |
1Cr-1/2Mo |
11/2Cr-1/2Mo |
2Cr-1/2Mo |
21/4Cr-1Mo |
5Cr-1/2Mo |
7Cr-1/2Mo |
9Cr-1Mo |
18-8 |
|
碳 鋼 |
-- |
B |
C |
C |
D |
D |
D |
E |
E |
E |
A |
|
C-Mo |
B |
B |
C |
C |
D |
D |
D |
E |
E |
E |
A |
|
1/2Cr-1/2Mo |
C |
C |
C |
C |
D |
D |
D |
E |
E |
E |
A |
|
1Cr-1/2Mo |
C |
C |
C |
C |
D |
D |
D |
E |
E |
E |
A |
|
11/2Cr-1/2Mo |
D |
D |
D |
D |
D |
D |
D |
E |
E |
E |
A |
|
2Cr-1/2Mo |
D |
D |
D |
D |
D |
D |
D |
E |
E |
E |
A |
|
21/4Cr-1Mo |
D |
D |
D |
D |
D |
D |
D |
E |
E |
E |
A |
|
5Cr-1/2Mo |
E |
E |
E |
E |
E |
E |
E |
E |
E |
E |
F |
|
7Cr-1/2Mo |
E |
E |
E |
E |
E |
E |
E |
E |
E |
E |
F |
|
9Cr-1Mo |
E |
E |
E |
E |
E |
E |
E |
E |
E |
E |
F |
|
18-8 |
A |
A |
A |
A |
A |
A |
A |
F |
F |
F |
_ |
A- 通常不要求進(jìn)行焊后熱處理.
B- 當(dāng)含碳量超過0.2%,壁厚大于12毫米時(shí),需進(jìn)行熱處理:620-680℃, 壁厚每25毫米,保溫1小時(shí).
C- 壁厚大于50毫米時(shí)或管徑大于102毫米(管壁大于12毫米)時(shí):650-700℃,保溫1小時(shí)/每25毫米.
D- 壁厚大于50毫米時(shí)或管徑大于102毫米(管壁大于12毫米)時(shí):690-730℃,保溫1小時(shí)/每25毫米.
E- 加熱溫度:700-750℃,保溫1小時(shí)/每25毫米,預(yù)熱溫度須保持到進(jìn)行熱處理之前.
F- 壁厚大于12毫米時(shí), 加熱700-750℃,保溫1小時(shí)/每25毫米.