PETG塑膠原料T95韓國SKPETGT95
PETG塑膠原料T95韓國SKPETGT95
供應(yīng)簡介:
東莞市塑膠原料有限公司
【一級總代理】
詳細(xì)說明：
| 物理性能 |
額定值
|
單位制
|
測試方法
|
|
比重
|
|||
|
--
|
1.27
|
|
ASTM D792 |
|
73°F
|
1.27
|
g/cm3
|
ISO 1183/D |
|
--
|
1.27
|
g/cm3
|
ASTM D1505 |
|
吸水率 (73°F, 24 hr)
|
0.13
|
%
|
ASTM D570, ISO 62 |
| 硬度 |
額定值
|
單位制
|
測試方法
|
|
洛氏硬度
|
|||
|
R 級, 73°F
|
106
|
|
ASTM D785 |
|
R 計秤, 73°F
|
109
|
|
ISO 2039-2 |
| 機(jī)械性能 |
額定值
|
單位制
|
測試方法
|
|
拉伸模量 (73°F)
|
305000
|
psi
|
ASTM D638, ISO 527-2 |
|
抗張強(qiáng)度
|
ASTM D638, ISO 527-2 | ||
|
屈服, 73°F
|
7250
|
psi
|
|
|
斷裂, 73°F
|
4060
|
psi
|
|
|
伸長率
|
|||
|
斷裂, 73°F
|
130
|
%
|
ASTM D638 |
|
斷裂, 73°F
|
100
|
%
|
ISO 527-2 |
|
彎曲模量
|
|||
|
73°F
|
305000
|
psi
|
ASTM D790 |
|
73°F
|
290000
|
psi
|
ISO 178 |
|
彎曲應(yīng)力
|
|||
|
73°F
|
9860
|
psi
|
ISO 178 |
|
屈服, 73°F
|
10200
|
psi
|
ASTM D790 |
|
撕裂阻力
|
ASTM D2582 | ||
|
MD : 73°F, 9.8 mil
|
93
|
N
|
|
|
TD : 73°F, 9.8 mil
|
93
|
N
|
|
| 薄膜 |
額定值
|
單位制
|
測試方法
|
|
薄膜厚度 - 經(jīng)測試
|
9.8
|
mil
|
|
|
割線模量
|
ASTM D882 | ||
|
MD : 9.8 mil
|
276000
|
psi
|
|
|
TD : 9.8 mil
|
276000
|
psi
|
|
|
抗張強(qiáng)度
|
ASTM D882 | ||
|
MD : 屈服, 9.8 mil
|
7540
|
psi
|
|
|
TD : 屈服, 9.8 mil
|
7540
|
psi
|
|
|
MD : 斷裂, 9.8 mil
|
8560
|
psi
|
|
|
TD : 斷裂, 9.8 mil
|
7980
|
psi
|
|
|
伸長率
|
ASTM D882 | ||
|
MD : 屈服, 9.8 mil
|
4.0
|
%
|
|
|
TD : 屈服, 9.8 mil
|
4.0
|
%
|
|
|
MD : 斷裂, 9.8 mil
|
400
|
%
|
|
|
TD : 斷裂, 9.8 mil
|
400
|
%
|
|
|
落錘沖擊 3
|
ASTM D1709A | ||
|
0°F, 9.8 mil
|
500
|
g
|
|
|
73°F, 9.8 mil
|
400
|
g
|
|
|
埃爾曼多夫抗撕強(qiáng)度
|
ASTM D1922 | ||
|
MD : 9.8 mil
|
1400
|
g
|
|
|
TD : 9.8 mil
|
1700
|
g
|
|
|
褲型撕裂耐性 4
|
ISO 6383-1 | ||
|
MD
|
206
|
lbf/in
|
|
|
TD
|
206
|
lbf/in
|
|
|
透氧率 (73°F, 9.8 mil, 50% RH)
|
25
|
cm3·mil/100in2/atm/24 hr
|
ASTM D3985 |
|
水氣透過率 (100°F, 100% RH, 9.8 mil)
|
0.45
|
g/100 in2/24 hr
|
ASTM F1249 |
|
Carbon Dioxide Permeability (73°F, 9.8 mil)
|
120
|
cm3·mil/100in2/atm/24 hr
|
ASTM D1434 |
|
抗撕裂蔓延性 5
|
ASTM D1938 | ||
|
MD : 73°F, 9.8 mil
|
210
|
lbf/in
|
|
|
TD : 73°F, 9.8 mil
|
210
|
lbf/in
|
|
| 沖擊性能 |
額定值
|
單位制
|
測試方法
|
|
懸壁梁缺口沖擊強(qiáng)度
|
|||
|
-40°F
|
0.69
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
1.9
|
ft·lb/in
|
ASTM D256 |
|
-40°F
|
2.0
|
ft·lb/in2
|
ISO 180/1A |
|
73°F
|
3.0
|
ft·lb/in2
|
ISO 180/1A |
|
無缺口懸臂梁沖擊
|
|||
|
-40°F, 0.126 in
|
無斷裂
|
|
ASTM D4218 |
|
-22°F, 0.126 in
|
無斷裂
|
|
ASTM D4218 |
|
-4°F, 0.126 in
|
無斷裂
|
|
ASTM D4218 |
|
73°F, 0.126 in
|
無斷裂
|
|
ASTM D4218 |
|
-40°F 6
|
無斷裂
|
|
ISO 180/1U |
|
-22°F 6
|
無斷裂
|
|
ISO 180/1U |
|
-4°F 6
|
無斷裂
|
|
ISO 180/1U |
|
73°F 6
|
無斷裂
|
|
ISO 180/1U |
|
裝有測量儀表的落鏢沖擊
|
|||
|
-40°F, 0.0984 in, Energy at Peak Load
|
363
|
in·lb
|
ASTM D3763 |
|
-40°F, 0.126 in, Energy at Peak Load
|
443
|
in·lb
|
ASTM D3763 |
|
73°F, 0.0984 in, Energy at Peak Load
|
248
|
in·lb
|
ASTM D3763 |
|
73°F, 0.126 in, Energy at Peak Load
|
292
|
in·lb
|
ASTM D3763 |
|
-40°F, 0.0984 in, 能量到力量峰值 7, 8
|
25.8
|
ft·lb
|
ISO 6603-2 |
|
-40°F, 0.126 in, 能量到力量峰值 7, 8
|
26.6
|
ft·lb
|
ISO 6603-2 |
|
73°F, 0.0984 in, 能量到力量峰值 7, 8
|
29.5
|
ft·lb
|
ISO 6603-2 |
|
73°F, 0.126 in, 能量到力量峰值 7, 8
|
32.5
|
ft·lb
|
ISO 6603-2 |
財富熱線：
聯(lián) 系 人： 葉海蓮
聯(lián)系電話： 138-25737859
QQ: 3459058209
PETG是一種非結(jié)晶性共聚酯。在其生產(chǎn)過程中，由于一定數(shù)量的乙二醇被1，4-cyclohexane dimethanol(CHDM)所取代，可預(yù)防結(jié)晶化，進(jìn)而改善加工制造和透明度。其制品高度透明，抗沖擊性能優(yōu)異，特別適宜成型厚壁透明制品，其加工成型性能佳，能夠按照設(shè)計者的意圖進(jìn)行任意形狀的設(shè)計，可能采用傳統(tǒng)的擠出、注塑、吹塑及吸塑等成型方法，可以廣泛用于板材、片材、高性能收縮膜、瓶用及異型材等市場，同時其二次加工性能優(yōu)良，可以進(jìn)行常規(guī)機(jī)加工修飾。
出眾的熱成型性能
PETG板材易于生產(chǎn)出造型復(fù)雜制品。而且，與PC板和抗沖改性的壓克力不同，這種板材無須在熱成型加工前進(jìn)行預(yù)干燥處理。與PC板或壓克力相比，其成型周期短，溫度低。
堅韌性
PETG板材的擠出板材通常比通用壓克力堅韌15至20倍，比抗沖改性的壓克力堅韌5至10倍。PETG板材在加工、運(yùn)輸和使用過程中具有足夠的承受能力，有助于防止破裂。
耐候性
PETG板材提供了優(yōu)秀的耐候性。它可以保持產(chǎn)品的堅韌性，防止變黃。它含有紫外線吸收劑，可共擠成一保護(hù)層，保護(hù)了板材免受紫外線的有害影響。
加工簡便
PETG板材可進(jìn)行鋸切、模切、鉆孔、沖孔、剪切、鉚接、銑邊以及冷彎，不至于破碎。表面的輕微刮痕可用熱風(fēng)槍來消除。溶劑粘接亦是常規(guī)操作。它比通用壓克力、抗沖改性壓克力或PC板更易于加工，并可進(jìn)行植絨、電鍍、靜電等加工處理。
優(yōu)秀的耐化學(xué)性能
PETG板材可以耐受多種化學(xué)品以及常用的清潔劑。
環(huán)保
PETG板材基材均為環(huán)保材料，符合食品接觸管理要求。
經(jīng)濟(jì)性
它比PC板便宜，比壓克力經(jīng)久耐用。
PETG板材
(1)板、片材
使用常規(guī)的成型方法，可以制備1~25.4mm厚的透明材料，具有突出的韌性和高抗沖擊強(qiáng)度，其抗沖擊強(qiáng)度是改性聚丙烯酸酯類的3~10倍，成型性能優(yōu)異，冷彎曲不泛白，無裂紋，易于印刷和修飾，廣泛應(yīng)用于室內(nèi)外標(biāo)牌、儲物架、自動售貨機(jī)面板、家具、建筑及機(jī)械擋板等。