陜西THD707堆焊焊條現貨
|
牌號 |
型號 GB |
焊絲化學成分（%）(≤) |
硬度 |
特點與用途 |
|||||||||||||||
|
C |
Mn |
Cr |
Mo |
Ni |
其余 |
HRC |
|||||||||||||
|
THY-QD5Cr8Si3 |
— |
0.7 |
— |
7.0/9.0 |
— |
— |
Si1.5-3 |
55 |
用于堆焊常溫及非腐蝕條件下磨粒磨損的零 |
||||||||||
|
THYQD3Cr2W8 |
— |
0.35/0.75 |
— |
2.0/3.5 |
— |
— |
W7.0-10 |
52 |
用于鍛模的修復 |
||||||||||
|
THY-QD127 |
— |
0.2 |
4.2 |
— |
— |
— |
— |
38 |
用于堆焊車軸、行走主動輪等 |
||||||||||
|
THY-QD-172 |
— |
0.5 |
— |
2.50 |
2.5 |
— |
— |
40 |
用于單層或多層堆焊各種受磨損的機件面 |
||||||||||
|
THY-QD212 |
— |
0.25/0.55 |
— |
5.0 |
0.5/1.5 |
— |
— |
50 |
用于單層或多層堆焊各種磨損的機件表面 |
||||||||||
|
THY-MD401-4 |
— |
0.1/0.2 |
0.8/1.5 |
4.0/70 |
0.6/1.2 |
— |
W0.8/1.6 |
45 |
配合HJ1017用于熱軋輥及坯輥的修復模的修復 |
||||||||||
|
THY-MD301-4 |
— |
0.06/0.20 |
0.8/2.0 |
1.1.0/15.0 |
0.6/2.0 |
1.2/2.5 |
1.5/2.5 |
40 |
用于15CrMo、30Cr3Mo等連鑄輥的修復及其復合軋輥的制造 |
||||||||||
|
THY-MD403L-4 |
— |
0.25/0.40 |
0.5/3.5 |
1.5/6.5 |
0.8/1.6 |
— |
0.5/3.0 |
50 |
用于9Cr2Mo，9Cr3Mo系列冷軋中間輥及冷軋工作輥的修復及其復合輥的制造 |
||||||||||
|
THY-MD451-4 |
— |
0.18/0.35 |
1.2/2.0 |
4.0/6.5 |
0.8/1.6 |
— |
1.0/1.8 |
45 |
用于9Cr2Mo，45Cr4NiMoV系列冷軋中間輥及冷軋工作輥的修復及其復合輥的制造 |
||||||||||
|
THY-MD556-4 |
— |
0.30/0.50 |
0.8/1.6 |
3.5/6.5 |
0.8/1.6 |
— |
W1.0-1.8 |
55 |
該焊絲配合焊接HJ107用于冷軋中間輥的表面堆焊 |
||||||||||
|
THY-MD404L-4 |
— |
0.04/0.07 |
0.5/3.5 |
1.5/6.5 |
0.8/3.0 |
— |
1-3.0 |
35 |
該焊絲配合焊接HJ107用于冷軋支撐輥和冷軋中間輥的過渡層堆焊 |
||||||||||
|
THY-ZD1Cr13Ni2W |
— |
0.20 |
7.0 |
10/13 |
— |
2.0/5.0 |
W0.6 |
32 |
自保護藥芯焊絲，用于車軸，齒輪行走主動輪的堆焊 |
||||||||||
|
牌號 |
型號 GB |
堆焊金屬化學成分(%)（≤） |
堆焊層硬度 |
特點與用途 |
|
||||||||||||||
|
C |
Mn |
Si |
S |
P |
其他 |
HRC |
|
||||||||||||
|
THD107 |
EDPMn2-15 |
0.20 |
3.50 |
— |
— |
— |
— |
HB220 |
用于堆焊或修復碳鋼、中碳鋼及低碳鋼磨損件的表面 |
|
|||||||||
|
THD112 |
EDPCrMo-A1-03 |
0.25 |
— |
Mo1.50 Cr2.00 |
HB220 |
用于堆焊或修復碳鋼、中碳鋼及低碳鋼磨損件的表面，特別適用于礦山機械、農業機械的堆焊與修補 |
|
||||||||||||
|
THD127 |
相當于EDPMn4-15 |
0.20 |
4.20 |
— |
28 |
用于堆焊受磨損中，低碳鋼或低合金鋼的表面 |
|
||||||||||||
|
THD132 |
EDPCrMo-A2-03 |
0.50 |
— |
Mo1.50 Cr3.00 |
30 |
用于堆焊受磨損中，低碳鋼或低合金鋼的表面 |
|
||||||||||||
|
THD146 |
EDPMn4-16 |
0.20 |
4.50 |
其它元素總量：2.00 |
30 |
用于堆焊各種受磨損的碳鋼的表面及碳鋼的道岔 |
|
||||||||||||
|
THD167 |
EDPMn6-15 |
0.45 |
6.50 |
1.00 |
— |
50 |
用于農業、建筑機械等的磨損部分的堆焊 |
|
|||||||||||
|
THD172 |
EDPCrMo-A3-03 |
0.50 |
— |
— |
Mo2.50 Cr2.50 |
40 |
用于堆焊齒輪、挖泥斗、拖拉機刮板和礦山機械等磨損件 |
|
|||||||||||
|
THD207 |
EDPCrMnSi-15 |
0.50/1.00 |
2.50 |
1.00 |
0.035 |
Cr3.50 |
50 |
用于堆焊推土機刀片、螺旋槳等磨損件 |
|
||||||||||
|
THD212 |
EDPCrMo-A4-03 |
0.30/0.60 |
— |
— |
— |
Mo4.00 Cr5.00 |
50 |
用于單層或多層堆焊各種受磨損機件表面，如齒輪、礦山機械等 |
|
||||||||||
|
THD256 |
EDMn-A-16 |
1.10 |
11.00/16.00 |
1.30 |
— |
其他元素總量：5.00 |
HB170 |
高錳鋼堆焊 |
|
||||||||||
|
THD266 |
EDMn-B-16 |
1.10 |
11.00/18.00 |
0.30/1.30 |
— |
— |
Mo2.50 |
HB170 |
高錳鋼堆焊 |
|
|||||||||
|
THD276 |
EDCrMn-B-16 |
0.80 |
11.00/16.00 |
0.80 |
|
|
Cr13.00/17.00 Ni≤2.0 Mo≤2.0 |
HB210 |
耐氣蝕和高錳鋼堆焊 |
|
|||||||||
|
THD307 |
EDD-D-15 |
0.70/1.00 |
— |
— |
0.035 |
0.035 |
V1.00/1.50 Cr3.80/4.50 W17.00/19.50 |
55 |
高速鋼刀具堆焊 |
|
|||||||||
|
THD322 |
EDRCrMoWV-A1-03 |
0.50 |
|
|
0.035 |
0.035 |
Mo2.50 V1.00 Cr5.00 W7.00/10.00 |
55 |
冷沖模及切削刀具堆焊 |
|
|||||||||
|
THD327 |
EDRCrMoWV-A1-15 |
0.50 |
|
|
0.035 |
0.035 |
Mo2.50 V1.00 Cr5.00 W7.00/10.00 |
55 |
冷沖模及切削刀具堆焊 |
|
|||||||||
|
THD337 |
EDRCrW-15 |
0.25/0.55 |
|
|
0.035 |
0.035 |
Cr2.00/3.50 W7.00/10.00 |
48 |
用于鑄鋼或鍛鋼上堆焊鍛模，也可用于修復鍛模 |
|
|||||||||
|
THD397 |
EDRCrMnMo-15 |
≤0.60 |
≤2.50 |
≤1.00 |
0.035 |
0.035 |
Mo1.00 Cr2.00 |
40 |
用于堆焊鑄鋼或鍛鋼作坯體的熱鍛模 |
|
|||||||||
|
THD397Ni |
— |
0.50/0.60 |
0.50/0.90 |
≤0.50 |
0.035 |
0.040 |
Mo0.15/0.30 Cr0.5/0.80 Ni1.0/2.0 |
40 |
用于堆焊鑄鋼或鍛鋼作坯體的熱鍛模 |
|
|||||||||
|
THD507Mo |
EDCr-A2-15 |
0.20 |
— |
— |
— |
— |
Cr10.00/16.00 Ni6.00 Mo2.50 W2.00 其它元素總量2.50 |
37 |
用于堆焊工作溫度在510℃以下的中溫高壓截止閥密封面。 |
|
|||||||||
|
THD512 |
EDCr-B-03 |
≤0.25 |
— |
— |
0.035 |
0.035 |
Cr10.00/16.00 |
45 |
通用性的表面堆焊用焊條，用于堆焊碳鋼或低合金鋼的軸，中高壓閥門等。 |
|
|||||||||
|
THD516M |
EDCrMn-A-16 |
0.25 |
0.60/8.00 |
1.00 |
— |
— |
Cr12.00/14.00 |
30 |
用于堆焊工作溫度在450℃以下受水、蒸汽、石油介質作用下的部件。 |
|
|||||||||
|
ThD516F |
相當于EDCrMn-A-16 |
0.25 |
8.0/1.00 |
1.00 |
— |
— |
Cr12.00/14.00 |
35～45 |
用于堆焊工作溫度在450℃以下受水、蒸汽、石油介質作用下的部件。 |
|
|||||||||
|
THD517 |
EDCr-B-15 |
0.25 |
— |
— |
|
|
Cr10.00/16.00 |
45 |
一種通用性的表面堆焊用焊條，用于堆焊碳鋼或低合金鋼的軸、蒸汽閥門等。 |
|
|||||||||
|
THD547Mo |
EDCr-B-15 |
0.18 |
0.60/5.00 |
3.80/6.50 |
0.030 |
0.040 |
Cr14.00/21.00 Mo3.50/7.00 Ni6.50/12.00 |
37 |
工作溫度低于600℃的高壓閥門密封面的堆焊 |
|
|||||||||
|
THD547MoA |
— |
0.18 |
1.00/ 2.50 |
2.00/3.20 |
0.03 |
0.04 |
Cr14.00/20.00 Ni8.00/12.50 Mo3.50/7.00 Nb0.50/1.20 W2.80 V1.50 |
37 |
用于工作溫度低于600℃的高壓閥門密封面的堆焊。 |
|
|||||||||
|
THD608 |
EDZ-A1-08 |
2.50/4.50 |
— |
— |
— |
— |
Mo3.00/5.00 Cr3.00/5.00 |
55 |
用于農業機械、礦山設備等承受沙粒磨損與輕擊的零件 |
|
|||||||||
|
THD618 |
— |
4.00 |
— |
— |
0.03 |
0.04 |
Cr15.00/20.00 Mo3.00/6.50 |
58 |
可用于常溫中耐泥沙汽蝕等條件下的零件堆焊。 |
|
|||||||||
|
THD642 |
EDZCr-B-03 |
1.50/3.50 |
1.00 |
|
|
|
Cr22.00/32.00 其他元素總量：7.00 |
45 |
用于常溫和高溫耐磨耐腐蝕的工作條件 |
|
|||||||||
|
THD667 |
EDZCr-C-15 |
2.50/5.00 |
8.00 |
1.00/4.80 |
|
|
Cr25.00/32.00 Ni3.00/5.00 |
48 |
耐強烈磨損，耐腐蝕或耐氣蝕的堆焊 |
|
|||||||||
|
THD707 |
EDW-A-15 |
1.50/3.00 |
2.00 |
4.00 |
— |
— |
W40.00/50.00 Fe 余量 |
60 |
適于 |
|
|||||||||