磨砂玻璃填充PEI ULTEM 2212EPR
ULTEM ? Resin 2212EPR |
PEI 基礎創新塑料（美國）2212EPR
ULTEM 2212EPR
20%磨碎的玻璃（帶壓花玻璃纖維）填充，增強流動Polyetherimide(Tg 217 c)與內部脫模。符合ECO，阻燃UL94-V0和5VA等級。
典型屬性：
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 1090 | kgf/cm2 | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 1090 | kgf/cm2 | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 59000 | kgf/cm2 | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1750 | kgf/cm2 | ASTM D 790 |
| Flexural Stress, brk, 2.6 mm/min, 100 mm span | 1750 | kgf/cm2 | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 56200 | kgf/cm2 | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 52000 | kgf/cm2 | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 49 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact, notched, 23°C | 5 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 124 | cm-kgf | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 210 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 210 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 212 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 207 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.4 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method |
| Melt Flow Rate, 337°C/6.6 kgf | 15 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.4 | mm | UL 94 |
聚醚酰亞胺PEI （Polyetherimide），PEI 是琥珀色透明固體，不添加任何添加劑PEI原料顆粒圖片就有固有的阻燃性和低煙度，氧指數為47%，燃燒等級為UL94-V-0級，密度為1.28~1.42g/cm3。PEI具有很強的高溫穩定性，即使是非增強型的PEI，仍具有很好的韌性和強度。因此利用PEI優越的熱穩定性可用來制作高溫耐熱器件。具有優良的機械性能、電絕緣性能、耐輻照性能、耐高低溫及耐磨性能，并可透過微波。
PEI(聚醚酰亞胺)具有優良的機械性能、電絕緣性能、耐輻照性能、耐高低溫及耐磨性能，并可透過微波。PEI兼具優良的高溫機械性能和耐磨性，故可用于制造輸水管轉向閥的閥件。由于具有很高的強度、柔韌性和耐熱性，PEI是優良的涂層和成膜材料，能形成適用于電子工業的涂層和薄膜。 主要特點 連續工作溫度范圍大（-200--170度長期工作），玻璃化溫度與熱變性溫度接近、熔點高達330度 在低溫/高溫下仍保有高機械強度、高硬度、高抗蠕變性、良好韌性 杰出的抗析出性 ( 適合用在利用蒸氣消毒的殺菌室 )；不易滋生細菌，常用于食品加工業 高抗輻射性優異、可透過紅外光和微波輻射；電器絕緣性好、良好的電鍍性能 較寬溫度（-200--170度）范圍保持穩定的介電常數和損耗因數 不能通過SMT回流焊接測試 主要應用 電子行業：連接件、普通和微型繼電器外殼、電路板、線圈、軟性電路、反射鏡、高精度密光纖元件、高溫隔熱板 汽車行業：連接件、高功率車燈和指示燈、控制汽車艙室外部溫度的傳感器、控制空氣和燃料混合物溫度的傳感器，醫 療器材等。