玻纖35填充尼龍6 德國(guó)巴斯夫 B3EG7
PA6 德國(guó)巴斯夫 B3EG7
BASF Ultramid B3EG7 35% Glass Filled PA6 (Dry)
產(chǎn)品說(shuō)明：35%玻璃纖維增強(qiáng)注塑級(jí)，工業(yè)應(yīng)用和電絕緣零件。
物理性能：
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |
| Density | 1.41 g/cc | 0.0509 lb/in3 | ISO 1183 |
| Water Absorption | 5.9 - 6.5 % | 5.9 - 6.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | >= 2.0 % | >= 2.0 % | 50% RH |
| 1.8 - 2.2 % | 1.8 - 2.2 % | ISO 62 | |
| >= 6.2 % | >= 6.2 % | Saturation | |
| Viscosity Measurement | 140 | 140 | ISO 307 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | |
| Melt Flow |
63.45 g/10 min @Load 5.00 kg, Temperature 275 °C |
63.45 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
機(jī)械機(jī)械：
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-1/-2 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527-1/-2 |
| Flexural Strength | 280 MPa | 40600 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) |
19.0 kJ/m2 @Temperature 23.0 °C |
9.04 ft-lb/in2 @Temperature 73.4 °F |
ISO 180/1A |
Charpy Impact Unnotched 
|
9.00 J/cm2 @Temperature -30.0 °C |
42.8 ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eU |
|
10.0 J/cm2 @Temperature 23.0 °C |
47.6 ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eU | |
|
Charpy Impact, Notched
|
1.30 J/cm2 @Temperature -30.0 °C |
6.19 ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eA |
|
1.80 J/cm2 @Temperature 23.0 °C |
8.57 ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eA |