30%玻璃纖維/玻璃珠填充PA6 德國朗盛 BG30X
PA6 德國朗盛 BG30X
Lanxess Durethan BG 30 X W1 000000 Nylon 6, Glass Fiber Reinforced
性能特點：30%玻璃纖維/玻璃珠填充增強PA6,注塑、低翹曲，耐候。
物理性能：
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in3 | ISO 60 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.0 % | 7.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0030 cm/cm | 0.0030 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0030 cm/cm | 0.0030 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
熱性能：
| CTE, linear, Parallel to Flow |
30.0 μm/m-°C @Temperature 23.0 - 55.0 °C |
16.7 μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow |
90.0 μm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1, -2 |
| Vicat Softening Point |
>= 200 °C @Load 5.10 kg |
>= 392 °F @Load 11.2 lb |
120°C/hour; ISO 306 |