高玻纖填充PA6 德國(guó)朗盛 DPBKV60EF 000000
PA6 德國(guó)朗盛 DPBKV60EF 000000
Lanxess Durethan DP BKV 60 EF 000000 Nylon6, 60% Glass Fiber
產(chǎn)品說(shuō)明：PA6,60%玻璃纖維填充,注射成型,改善流動(dòng)性。
機(jī)械性能：
| Tensile Strength at Break | 158 MPa | 22900 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 230 MPa | 33400 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 2.5 % | 2.5 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 3.5 % | 3.5 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 12.5 GPa | 1810 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 20.0 GPa | 2900 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength |
390 MPa @Strain 3.00 % |
56600 psi @Strain 3.00 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Modulus | 20.2 GPa | 2930 ksi | d.a.m., 2 mm/min; ISO 178-A |
Izod Impact, Notched (ISO) 
|
18.0 kJ/m2 @Temperature 23.0 °C |
8.57 ft-lb/in2 @Temperature 73.4 °F |
d.a.m.; ISO 180-1A |
|
18.0 kJ/m2 @Temperature -30.0 °C |
8.57 ft-lb/in2 @Temperature -22.0 °F |
cond.; ISO 180-1A | |
|
Izod Impact, Unnotched (ISO)
|
90.0 kJ/m2 @Temperature 23.0 °C |
42.8 ft-lb/in2 @Temperature 73.4 °F |
d.a.m.; ISO 180-1U |
|
90.0 kJ/m2 @Temperature 23.0 °C |
42.8 ft-lb/in2 @Temperature 73.4 °F |
cond.; ISO 180-1U | |
|
90.0 kJ/m2 @Temperature -30.0 °C |
42.8 ft-lb/in2 @Temperature -22.0 °F |
d.a.m.; ISO 180-1U | |
|
90.0 kJ/m2 @Temperature -30.0 °C |
42.8 ft-lb/in2 @Temperature -22.0 °F |
cond.; ISO 180-1U | |
|
Charpy Impact Unnotched
|
9.50 J/cm2 @Temperature 23.0 °C |
45.2 ft-lb/in2 @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU |
|
9.50 J/cm2 @Temperature -30.0 °C |
45.2 ft-lb/in2 @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
|
Charpy Impact, Notched
|
1.70 J/cm2 @Temperature 23.0 °C |
8.09 ft-lb/in2 @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA |
|
1.70 J/cm2 @Temperature -30.0 °C |
8.09 ft-lb/in2 @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA | |
|
Puncture Energy
|
3.70 J @Load <=133 kg, Temperature -30.0 °C |
2.73 ft-lb @Load <=292 lb, Temperature -22.0 °F |
ISO 6603-2 |
|
4.30 J @Load <=140 kg, Temperature 23.0 °C |
3.17 ft-lb @Load <=308 lb, Temperature 73.4 °F |
ISO 6603-2 | |