導熱礦物填充尼龍6 美國液氮 PX11311
PA6 美國液氮 PX11311 WH9F059
SABIC Innovative Plastics LNP KONDUIT PX11311 PA 6
性能特點：導熱礦物填充尼龍6，FR阻燃化合物。阻燃UL94-V0.
物理性能：
| Density | 1.74 g/cc | 0.0629 lb/in3 | ASTM D792 |
| Water Absorption |
0.25 % @Time 86400 sec |
0.25 % @Time 24.0 hour |
SABIC Method |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0033 cm/cm @Time 86400 sec |
0.0033 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.0048 cm/cm @Time 86400 sec |
0.0048 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Index of Compound |
49 g/10 min @Load 10.0 kg, Temperature 300 °C |
49 g/10 min @Load 22.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
熱性能：
CTE, linear, Parallel to Flow 
19.4 μm/m-°C
@Temperature 40.0 - 120 °C10.8 μin/in-°F
@Temperature 104 - 248 °FASTM E 831 31.3 μm/m-°C
@Temperature -40.0 - 40.0 °C17.4 μin/in-°F
@Temperature -40.0 - 104 °FASTM E 831CTE, linear, Transverse to Flow 45.9 μm/m-°C
@Temperature -40.0 - 40.0 °C25.5 μin/in-°F
@Temperature -40.0 - 104 °FASTM E 831 69.5 μm/m-°C
@Temperature 40.0 - 120 °C38.6 μin/in-°F
@Temperature 104 - 248 °FASTM E 831Specific Heat Capacity 1.42 J/g-°C0.339 BTU/lb-°FASTM C351Thermal Conductivity 0.990 W/m-K6.87 BTU-in/hr-ft2-°Fthrough-plane, ?80*3mm discs; ISO 22007-2 1.20 W/m-K8.33 BTU-in/hr-ft2-°Fthrough-plane, 10*10*3mm sample; ASTM E 1461-07 1.38 W/m-K9.58 BTU-in/hr-ft2-°Fin-plane, ?80*3mm discs; ISO 22007-2 2.10 W/m-K14.6 BTU-in/hr-ft2-°Fin-plane, ?25*0.4mm disc; ASTM E 1461-07Deflection Temperature at 1.8 MPa (264 psi) 199 °C
@Thickness 6.40 mm390 °F
@Thickness 0.252 inunannealed; ASTM D648Flammability, UL94 V-0
@Thickness 1.00 mmV-0
@Thickness 0.0394 inUL 94Glow Wire Test 775 °C1430 °FIEC 60695-2-13 850 °C1560 °FIEC 60695-2-13 960 °C
@Thickness 1.00 - 3.00 mm1760 °F
@Thickness 0.0394 - 0.118 inIEC 60695-2-12