導(dǎo)熱耐候級PA6 美國液氮 PX08322
PA6 美國液氮 PX08322
SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6
LNP Konduit PX08322 礦物填充尼龍6化合物，導(dǎo)熱性和阻燃性能。阻燃UL94-V0，通過F1。
物理性能：
| Density | 1.52 g/cc | 0.0549 lb/in3 | ASTM D792 |
| Water Absorption |
0.39 % @Time 86400 sec |
0.39 % @Time 24.0 hour |
SABIC Method |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.0045 cm/cm @Time 86400 sec |
0.0045 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow |
15.3 g/10 min @Load 6.70 kg, Temperature 285 °C |
15.3 g/10 min @Load 14.8 lb, Temperature 545 °F |
ASTM D1238 |
熱性能：
CTE, linear, Parallel to Flow 
|
21.5 μm/m-°C @Temperature -40.0 - 40.0 °C |
11.9 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
27.1 μm/m-°C @Temperature 40.0 - 120 °C |
15.1 μin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 | |
|
CTE, linear, Transverse to Flow
|
35.4 μm/m-°C @Temperature -40.0 - 40.0 °C |
19.7 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
58.3 μm/m-°C @Temperature 40.0 - 120 °C |
32.4 μin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 | |
| Thermal Conductivity | 0.920 W/m-K | 6.38 BTU-in/hr-ft2-°F | through-plane, ?80*3mm discs; ISO 22007-2 |
| 2.10 W/m-K | 14.6 BTU-in/hr-ft2-°F | through-plane, 10*10*3mm sample; ASTM E 1461-07 | |
| 5.09 W/m-K | 35.3 BTU-in/hr-ft2-°F | in-plane, ?80*3mm discs; ISO 22007-2 | |
| 8.10 W/m-K | 56.2 BTU-in/hr-ft2-°F | in-plane, ?25*0.4mm disc; ASTM E 1461-07 | |
| Deflection Temperature at 1.8 MPa (264 psi) |
180 °C @Thickness 6.40 mm |
356 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 |
V-0 @Thickness 1.20 mm |
V-0 @Thickness 0.0472 in |
UL 94 |
| Glow Wire Test | 825 °C | 1520 °F | IEC 60695-2-13 |
|
960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-1 |