超級增韌聚酰胺66 Zytel ST801
PA66 美國杜邦 ST801
DuPont Performance Polymers Zytel ST801 NC010A Nylon 66物理性能：
| Density | 1.08 g/cc | 0.0390 lb/in3 | DAM; ISO 1183 |
| Water Absorption |
6.7 % @Thickness 2.00 mm |
6.7 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Moisture Absorption |
2.20 % @Thickness 2.00 mm |
2.20 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | DAM; ISO 294-4 2577 |
熱性能：
| CTE, linear, Parallel to Flow | 120 μm/m-°C | 66.7 μin/in-°F | DAM; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C | 50.0 μin/in-°F | DAM; ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | DAM; ISO 75-1/-2 |
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | DAM; 10°C/min; ISO 11357-1/-2 |
Flammability, UL94 
|
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 |
|
HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; IEC 60695-11-10 | |
| Flame Spread |
26 mm/min @Thickness 1.00 mm |
1.0 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) |
| Oxygen Index | 20 % | 20 % | DAM; ISO 4589-1/-2 |