經增強和PTFE潤滑尼龍66 美國LNP RFL36S
PA66 美國液氮 RFL36S
玻璃纖維增強 添加PTFE潤滑劑 熱穩定劑 ROHS合規 (RFL-4036HS)
SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66
LNP * lubricomp rfl36s是一種化合物，尼龍66樹脂含有30%的玻璃纖維，15%的聚四氟乙烯。這種材料的性能特點：耐磨，熱穩定。
比重：1.51
機械性能：
| Tensile Strength at Break | 138 MPa | 20000 psi | ISO 527 |
| 139 MPa | 20200 psi | ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527 |
| 2.1 % | 2.1 % | ASTM D638 | |
| Flexural Strength | 211 MPa | 30600 psi | ISO 178 |
| 236 MPa | 34200 psi | ASTM D790 | |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ISO 178 |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.58 | 0.58 | ASTM D3702 Modified |
| K (wear) Factor | 24.2 x 10-8 mm3/N-M | 12.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |