高沖擊尼龍66 LNP THERMOTUF V1000
PA66 美國液氮 V-1000
抗撞擊性高LNP THERMOTUF * V1000基于尼龍樹脂為基材的一種混合物。這種材料額外的特性包括:高沖擊。
物理性能：
| Density | 1.07 g/cc | 0.0387 lb/in3 | ISO 1183 |
| 1.073 g/cc | 0.03876 lb/in3 | ASTM D792 | |
| Moisture Absorption | 0.800 % | 0.800 % | 50% RH, 24 hrs; ASTM D570 |
| 1.37 % | 1.37 % | 23°C / 50% RH; ISO 62 | |
Linear Mold Shrinkage, Flow 
|
0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ASTM D955 |
|
0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ISO 294 | |
|
Linear Mold Shrinkage, Transverse
|
0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ASTM D955 |
|
0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ISO 294 |
機械性能：
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| 50.0 MPa | 7250 psi | ISO 527 | |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ISO 527 |
| 45.0 MPa | 6530 psi | ASTM D638 | |
| Elongation at Break | 60.3 % | 60.3 % | ASTM D638 |
| 168.1 % | 168.1 % | ISO 527 | |
| Elongation at Yield | 4.6 % | 4.6 % | ASTM D638 |
| 17.1 % | 17.1 % | ISO 527 | |
| Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527 |
| 1.93 GPa | 280 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| 74.0 MPa | 10700 psi | ASTM D790 | |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| 1.93 GPa | 280 ksi | ASTM D790 | |
| Izod Impact, Notched (ISO) | 84.0 kJ/m2 | 40.0 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 137 kJ/m2 | 65.2 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 56.0 J | 41.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 77.0 J | 56.8 ft-lb | Multiaxial Impact; ISO 6603 |