耐磨損低摩擦PPS Ryton BR42B
PPS 美國雪佛龍菲利普 BR42B
玻纖40％填充，低摩擦系數(shù) 耐磨損性好
美國雪佛龍菲利普PPS Ryton BR42B
Chevron Phillips Ryton BR42B Polyphenylene Sulfide Compound
特性：Ryton BR42B 是 40%玻璃纖維增強聚苯硫醚復(fù)合特別配方，使用低摩擦系數(shù)在低表面的摩擦和磨損的應(yīng)用程序。有 0.001 毫米/小時按 ASTM D3702 磨損率。
應(yīng)用范圍： 水泵葉片。
機械性能：
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Yield Strength | 275 MPa | 39900 psi | ASTM D790 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
| Compressive Yield Strength | 205 MPa | 29700 psi | ASTM D695 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.90 J/cm | 12.9 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | Against 52100 steel; 100 hours; 22.7 kg load (1.7 MPa); 36 RPM; Dry; Ambient Temperature; PV=2500; ASTM D3702 |