牌號 |
焊絲化學(xué)成分(wt.%) |
|||||||||
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Cu |
其它 |
|
|
TGF308 |
≤0.08 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
19.5-22.0 |
9.0-11.0 |
≤0.75 |
≤0.75 |
— |
|
TGF308L |
≤0.03 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
19.5-22.0 |
9.0-11.0 |
≤0.75 |
≤0.75 |
— |
|
TGF308H |
0.04-0.08 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
19.5-22.0 |
9.0-11.0 |
≤0.75 |
≤0.75 |
— |
|
TGF309 |
≤0.12 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
23.0-25.0 |
12.0-14.0 |
≤0.75 |
≤0.75 |
— |
|
TGF309L |
≤0.03 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
23.0-25.0 |
12.0-14.0 |
≤0.75 |
≤0.75 |
— |
|
TGF316 |
≤0.08 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
18.0-20.0 |
11.0-14.0 |
2.0-3.0 |
≤0.75 |
— |
|
TGF316L |
≤0.03 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
18.0-20.0 |
11.0-14.0 |
2.0-3.0 |
≤0.75 |
— |
|
TGF316H |
0.04-0.08 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
18.0-20.0 |
11.0-14.0 |
2.0-3.0 |
≤0.75 |
— |
|
TGF347 |
≤0.08 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
19.5-21.5 |
9.0-11.0 |
≤0.75 |
≤0.75 |
Nb: 10×C-1.0 |
|
TGF347H |
0.04-0.08 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
19.5-21.5 |
9.0-11.0 |
≤0.75 |
≤0.75 |
Nb: 10×C-1.0 |
|
TGF309LMo |
≤0.03 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
23.0-25.0 |
12.0-14.0 |
2.0-3.0 |
≤0.75 |
— |
|
TGF310 |
0.08- 0.15 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
25.0-28.0 |
20.0-22.5 |
≤0.75 |
≤0.75 |
— |
|
TGF317 |
≤0.08 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
18.5-20.5 |
13.0-15.0 |
3.0-4.0 |
≤0.75 |
— |
|
TGF317L |
≤0.03 |
0.30-0.65 |
1.0-2.5 |
≤0.03 |
≤0.03 |
18.5-20.5 |
13.0-15.0 |
3.0-4.0 |
≤0.75 |
— |
|
TGF385 |
≤0.025 |
≤0.50 |
1.0-2.5 |
≤0.03 |
≤0.03 |
19.5-21.5 |
24.0-26.0 |
4.2-5.2 |
1.2-2.0 |
— |
|
TGF2209 |
≤0.03 |
≤0.90 |
0.50-2.00 |
≤0.03 |
≤0.03 |
21.5-23.5 |
7.5-9.5 |
2.5-3.5 |
≤0.75 |
N: 0.08-0.20 |
|
TGF2594 |
≤0.03 |
≤1.00 |
≤2.50 |
≤0.03 |
≤0.02 |
24.0-27.0 |
8.0-10.5 |
2.5-4.5 |
≤1.50 |
W: ≤1.0 N: 0.20-0.30 |