| 管狀焊絲 | 焊劑 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | Mo | Mn | Fe | W | Ni | V | B | 其他 | | Delcrome 103 | 107 | 54 | 5.15 | 27.50 | 1.50 | | 2.50 | Bal | | | | | | 磨煤輥 | | Multipass 104 | 431 | 28 | 0.25 | 1.20 | 1.50 | | 3.00 | Bal | | | | | | 軋輥等堆焊過渡層及軸的修復 | | Multipass 105 | 431 | 45 | 0.50 | 4.00 | 1.10 | 0.50 | 2.75 | Bal | | | | | | 拖拉機惰輪、礦車輪、導輥 | | Multipass 107 | 431 | 37 | 0.35 | 2.70 | 1.20 | 0.25 | 2.70 | Bal | | | | | | 卷筒、拖拉機惰輪、礦車輪 | | Multipass 109 | 260 | | 0.45 | 3.10 | 0.60 | | 0.60 | Bal | | 0.5 | | | | 管模、鋁軋輥等 | | Multipass 224 | 107 | 46 | 0.45 | 5.50 | 0.65 | 1.10 | 1.80 | Bal | 1.50 | | | | | 各類軋輥及連鑄第3區(qū)輥 | | Multipass 224H | 107 | 53 | 0.55 | 6.50 | 0.65 | 1.10 | 1.80 | Bal | 1.50 | | | | 1.0 | 熱軋工作輥、支撐輥、開坯輥 | | Multipass 224HC | 107 | 58 | 0.75 | 7.70 | 0.75 | 1.80 | 1.70 | Bal | 2.60 | | | | 1.0 | 支撐輥、校直輥、助卷輥 | | Multipass 225 | 107 | 59 | 0.90 | 6.00 | 0.50 | 1.20 | 0.80 | Bal | 8.60 | | | | | 熱軋支撐輥 | | Multipass 235 | 107 | 60 | 0.45 | 9.00 | | 2.20 | 0.70 | Bal | 8.40 | Co:10.5 | 0.30 | | | 熱軋支撐輥 | | Multipass 236 | | | 0.28 | 3.10 | 0.70 | 2.00 | 0.70 | Bal | 1.90 | | 0.65 | | | 鋼管成型輥 | | Multipass 915 | 107 | 60 | 1.20 | 20.00 | 0.50 | | 0.70 | Bal | | | | 4.00 | | 高速磨打擊板等耐強沖擊，強磨粒磨損場合 | | Delstain 414-S | 260 | 40 | 0.20 | 14.00 | 0.50 | 1.00 | 1.40 | Bal | | 4.20 | | | | 連鑄輥等耐磨耐高溫場合 | | Delstain 420 | 260 | 46 | 0.40 | 13.00 | 0.50 | | 1.40 | Bal | | | | | | 一般軋鋼輥、剎車鼓、卷輥 | | Delstain 423 | 107 | 45 | 0.33 | 13.50 | 0.50 | 1.20 | 1.50 | Bal | | 2.50 | 0.20 | | | 連鑄機輥、熱軋輥堆焊 | | Delstain 424H | 260 | 49 | 0.40 | 12.00 | 0.50 | 0.90 | 2.20 | Bal | | 1.40 | | | | 有色工作輥的堆焊 | | Delstain 430 | 260 | | 0.10 | 19.00 | 0.50 | | 0.70 | Bal | | 0.60 | | | | 連鑄輥等耐磨耐高溫場合 | | Delcrome 911 | 107 | 57 | 6.60 | 36.50 | 0.40 | | 0.40 | Bal | | | | | | 磨煤輥堆焊 | | Delcrome 100HD | 107 | 57 | 6.80 | 29.00 | 1.00 | | 2.0 | Bal | | | | | Zr:0.45 | 磨煤輥等耐中等沖擊，強磨粒磨損場合 | | STW 101 | 431 | HB:250 | 0.25 | 1.35 | 0.55 | 0.60 | 1.35 | Bal | | | 0.25 | | | 碳鋼、低合金鋼部件修復 | | STW 102 | 431 | 36 | 0.25 | 2.95 | 0.55 | 1.00 | 1.00 | Bal | | 1.35 | 0.10 | | | 碳鋼、低合金鋼部件修復 | | STW 103 | | | 0.35 | 3.00 | 0.70 | 2.00 | 1.40 | Bal | | | 0.60 | | | 碳鋼、低合金鋼部件修復 | Multipass235司太立焊條，Multipass235司太立焊條， ， ， ， ， 五、提高焊接生產率，減少飛濺。焊條藥皮具有使熔滴增加而減少飛濺的作用。焊條藥皮的熔點稍低于焊芯的焊點，但因焊芯處于電弧的中心區(qū)，溫度較高，所以焊芯先熔化，藥皮稍遲一點熔化。這樣，在焊條端頭形成一短段藥皮套管，加上電弧吹力的作用，使熔滴徑直射到熔池上，使之有利于仰焊和立焊。另外，在焊芯涂了藥皮后，電弧熱量更集中。同時，由于減少了由飛濺引起的金屬損失，提高了熔敷系數(shù)，也就提高了焊接生產率。另外，焊接過程中發(fā)塵量也會減少。http://www.wanhonghanjie.com， ， （2）藥皮類型：鈦鈣型 ‖藥皮主要成分 ：氧化鈦30%以上，碳酸鹽20%以下 ‖焊接電源：直流或交流， ， 焊條牌號的編制方法 ， 焊條就是涂有藥皮的供焊條電弧焊使用的熔化電極，它是由藥皮和焊芯兩部分組成的。在焊條前端藥皮有45°左右的倒角，這是為了便于引弧。在尾部有一段裸焊芯，約占焊條總長1/16，便于焊鉗夾持并有利于導電。焊條的直徑實際上是指焊芯直徑）通常為2、2.5、3.2或3、4、5或6mm等幾種規(guī)格，最常用的是小3.2、小4、小5三種，其長度“l(fā)”一般在200～550 mm之間。， 焊芯的分類： ， 七、焊條藥皮類型及主要特點。按照藥皮的主要成分可以確定焊條的藥皮類型。由于藥皮配方組成不同，致使各種藥皮類型焊條的熔渣特性、焊接工藝性能以及焊縫金屬力學性能有很大差別。即使是同一類型藥皮，但不同牌號的焊條也因為藥皮成分和配比不同，焊條的工藝性能等也會出現(xiàn)明顯的差別。， ， ， ， | 管狀焊絲 | 硬度 | 化學成分（重量%） | 典型用途 | | Tungsmooth 60 | A-91 | 60%碳化鎢、其余為鋼管、A-91中的91為碳化鎢顆粒硬度 | 風機攪拌機葉片、采礦、建筑易損件 |
| 管狀焊絲 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | Mo | Mn | Fe | Ni | Al | 其他 | | Delcrome 11-o | 50 | 3.20 | 14.50 | 0.90 | 0.45 | 1.40 | Bal | | | | 破碎機錘頭、挖土機齒 | | Delcrome 94-o | 57 | 3.20 | 24.50 | 0.70 | | 0.80 | Bal | 2.80 | | | 筑路機零件、攪拌葉片 | | Delcrome 100-o | 57 | 3.80 | 26.50 | 1.40 | 1.30 | 1.90 | Bal | | | | 磨煤輥 | | Delcrome 100HC-o | 60 | 5.50 | 26.50 | 2.40 | 1.30 | 1.90 | Bal | | | | 磨煤輥、破碎輥 | | Delcrome 117-o | 43 | 2.30 | 10.50 | 1.30 | 1.50 | 1.50 | Bal | zr:0.40 | | Cu:0.40 | 破碎輥、錘頭 | | Delcrome 150-o | 58 | 2.20 | 7.00 | | 2.00 | 1.00 | Bal | V:0.20 | | Ti:7.00 | 水泥擠壓輥、錘頭、農具 | | Delcrome 945-o | 57 | 5.00 | 21.50 | 0.70 | 4.50 | 0.70 | Bal | W:2.00 | | Nb:7.00 | 高爐加料槽板、閘閥 | | Build up | 35 | 0.15 | 0.90 | 0.90 | 0.40 | 1.80 | Bal | | | | 碳鋼、低合金鋼恢復尺寸如齒輪、錘頭 | | Ni-Mang-o | 冷硬 | 0.85 | 3.00 | 0.50 | | 14.00 | Bal | 3.00 | | | 破碎機輥、顎板、挖泥機刀片 | | Sta-Mang-o | 冷硬 | 0.10 | 10.00 | 0.50 | 0.80 | 15.50 | Bal | 0.85 | | | 破碎機、鐵鏟、鐵路道岔 | | Multipass 4-o | 34 | 0.15 | 0.70 | 1.10 | 0.30 | 2.00 | Bal | | | | 碳鋼、低合金鋼部件修復 | | Multipass 5-o | 44 | 0.10 | 2.30 | 0.30 | 0.50 | 1.40 | Bal | | | | 拖拉機惰輪、起重機輪 | | Multipass 1265-g | 55 | 0.65 | 5.50 | 0.50 | 1.50 | 1.00 | Bal | W:1.50 | | V:0.30 | 冷沖壓模 | | Delcrome 90G | 48 | 2.40 | 24.00 | 0.60 | | 0.90 | Bal | | | | 鏟斗齒、排氣葉、提升斗 | | Delcrome 94G | 52 | 3.00 | 28.00 | 1.40 | | 1.20 | Bal | B:0.80 | | | 鏟斗齒、攪拌機、破碎輥 | | Mulitpass 106 | | 0.10 | | 0.90 | 5.20 | 1.40 | Bal | 5.20 | | | 管模，鋁軋輥等 | | Delcrome 165 | 62 | 6.80 | 30.00 | 3.00 | 0.50 | 0.50 | Bal | W:4.20 | | Nb:2.60 | 磨煤 輥等耐中等沖擊，強磨粒磨損場合 | | Delstain 414N-o | 47 | 0.20 | 14.00 | 0.50 | 1.00 | 1.30 | Bal | 4.20 | | N:0.22 | 連鑄輥等耐磨耐高溫場合 | | Delstain 431 | 33 | 0.40 | 17.50 | 0.50 | | 1.20 | Bal | | | | 連鑄輥等耐磨耐高溫場合 | | Delcrome 103HD | 60 | 5.60 | 30.00 | 1.10 | 0.80 | 1.20 | Bal | | | Cu:0.10 | 磨煤輥等 | | Stellarc 420 | 430（HV） | 0.3 | 13 | 1 | | 1 | Bal | | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 430 | 400（HV） | 0.7 | 17 | 1 | 0.5 | 1 | Bal | | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 316 | 240（HV） | 0.08 | 18 | 0.7 | 2.5 | 1 | Bal | 13 | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 100 | 660（HV） | 5 | 28 | 0.5 | | 1 | Bal | | | | 具有優(yōu)良的耐磨性 | | Stellarc 250 | | | 1 | 0.5 | 0.5 | 1 | Bal | | | WC:50 | 風機、風管、煙道內壁 | | Stellarc 45 | 400（HV） | | 45 | | | | | Bal | | | 風機、風管、煙道內壁 | | Stellarc 95 | 480（HV） | | | | | | | Bal | 5 | | 打底涂層 | | Stellarc 625 | 260（HV） | 0.08 | 21 | | 9 | | 5 | Bal | 5 | Nb+Ta:4 | 優(yōu)異的抗高溫腐蝕及耐磨介質 | | Stellarc 276 | | 0.08 | 16 | | 16 | | 5 | Bal | | W:4 | 耐腐蝕性能優(yōu)異，能抗硫酸、鹽酸或其他有機酸的腐蝕 | Multipass235司太立焊條，Multipass235司太立焊條， 1)碳(c)碳是鋼中的主要合金元素，當含碳量增加時，鋼的強度、硬度明顯提高，而塑性降低。在焊接過程中，碳起到一定的脫氧作用，在電弧高溫作用下與氧發(fā)生化合作用，生成一氧化碳和二氧化碳氣體，將電弧區(qū)和熔池周圍空氣排除，防止空氣中的氧、氮有害氣體對熔池產生的不良影響，減少焊縫金屬中氧和氮的含量。若含碳量過高，還原作用劇烈，會引起較大的飛濺和氣孔。考慮到碳對鋼的淬硬性及其對裂紋敏感性增加的影響，低碳鋼焊芯的含碳量一般為0. 1%。， 人們在實踐過程中發(fā)現(xiàn)如果在光焊條外面涂一層由各種礦物等組成的藥皮，能使電弧燃燒穩(wěn)定，焊縫質量得到提高，這種焊條叫藥皮焊條。隨著工業(yè)技術的不斷發(fā)展，人們創(chuàng)制出了廣泛應用的優(yōu)質厚藥皮焊條。http://www.wanhonghanjie.com， 此外，對于藥皮中含有多量鐵粉的焊條，可以稱為鐵粉焊條。這時，按照相應焊條藥皮的主要成分，又可分為鐵粉鈦型、鐵粉鈦鐵礦型、鐵粉氧化鐵型、鐵粉低氫型等，構成了鐵粉焊條系列。， 3)硅(si )硅也是一種較好的合金劑，在鋼中加入適量的硅能提高鋼的屈服強度、彈性及抗酸性能；若含量過高，則降低塑性和韌性。在焊接過程中，硅也具有較好的脫氧能力，與氧形成二氧化硅，但它會提高渣的粘度，易促進非金屬夾雜物生成。， (1)容易引弧，保證電弧穩(wěn)定，在焊接過程中飛濺小。， （10）藥皮類型：石墨型 ‖藥皮主要成分 ：多量石墨 ‖ 焊接電源：直流或交流， ， ，， 合金元素對焊接影響 ， 焊芯是根據(jù)國家標準“焊接用鋼絲”（gb 1300-77)的規(guī)定分類的，用于焊接的專用鋼絲可分為碳素結構鋼、合金結構鋼、不銹鋼三類。， ， 編輯， ， ， | 電焊條 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | B | Cu | 其他 | | Stellite 1 | 48 | 2.20 | 29.00 | 2.00 | 14.00 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 閥座、軸承、刀口等 | | Stellite 6 | 40 | 1.00 | 29.00 | 1.00 | 4.50 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 發(fā)動機氣門、高溫高壓閥門、渦輪機葉片 | | Stellite 12 | 44 | 1.30 | 29.00 | 1.00 | 9.00 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 高溫高壓閥門、鋸齒、螺旋推桿等 | | Stellite 21 | 23 | 0.30 | 28.00 | 1.00 | | 2.50 | 5.50 | 2.50 | Bal | 2.00 | | | | 渦輪機葉片、閥座、熱沖模 | | Stellite 25 | 冷硬 | 0.15 | 20.00 | 1.00 | 14.00 | 3.00 | 0.50 | 10.00 | Bal | 1.50 | | | | 高溫耐蝕密封面、擠壓模 | | Nistelle C | | 0.10 | 17.00 | | 5.00 | 6.00 | 17.00 | Bal | | | | | | 高溫耐蝕密封環(huán) | | Ni-Mang | 冷硬 | 0.60 | 2.70 | 0.20 | | Bal | | 3.70 | | 13.50 | | | | 錘式破碎機、高錳鋼部件焊接 | | STE 308-16 | | 0.08 | 19.50 | 0.90 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | | 用于焊接Cr18Ni8不銹鋼 | | STE 308L-16 | | 0.03 | 19.50 | 0.90 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | | 用于焊接超低碳Cr18Ni8不銹鋼 | | STE 309-16 | | 0.15 | 23.50 | 0.90 | | Bal | 0.50 | 13.00 | | 0.80 | | 0.50 | | 用于焊接Cr22Nil2不銹鋼及用于不銹鋼與低碳鋼或低合金鋼之間的焊接 | | STE 309L-16 | | 0.02 | 23.50 | 0.90 | | Bal | 0.50 | 13.00 | | 0.80 | | 0.50 | | 打底層焊接，異種鋼焊接，易產生裂紋部位的焊接 | | STE 309Mo-16 | | 0.12 | 23.50 | 0.90 | | Bal | 2.50 | 13.00 | | 0.80 | | | | 用于焊接Cr22Nil2-Mo不銹鋼 | | STE 309MoL-16 | | 0.03 | 23.50 | 0.90 | | Bal | 2.50 | 13.00 | | 0.80 | | | | 用于焊接超低碳Cr22Nil2Mo不銹鋼 | | STE 310-16 | | 0.20 | 26.50 | 0.75 | | Bal | 0.50 | 21.50 | | 1.50 | | 0.50 | | 用于焊接Cr25Ni20不銹鋼 | | STE 310Mo-16 | | 0.08 | 26.50 | 0.75 | | Bal | 2.50 | 21.00 | | 1.20 | | 0.50 | | 耐硫酸腐蝕、抗裂性、高溫性能優(yōu)良 | | STE 316-16 | | 0.05 | 18.50 | 0.90 | | Bal | 2.50 | 12.50 | | 0.80 | | 0.50 | | 用于焊接Cr18Ni12Mo2不銹鋼 | | STE 316L-16 | | 0.03 | 18.50 | 0.90 | | Bal | 2.50 | 12.50 | | 0.80 | | 0.50 | | 用于焊接超低碳Cr18Ni12Mo2不銹鋼 | | STE 316LF | | 0.02 | 18.00 | 0.75 | | Bal | 2.70 | 16.00 | | 2.00 | | 0.50 | | 耐尿素腐蝕性優(yōu)良 | | STE 347-16 | | 0.08 | 19.50 | 0.50 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | 8xc-1.00 | 用于焊接Cr18Ni8含鈮或鈦的不銹鋼 | | STE 997 | 56 | 0.60 | 5.50 | 0.80 | | Bal | 4.00 | W:7.0 | | 0.70 | | | | 低氫型高速鋼焊條 | | D 287 | 40 | 0.10 | 14.00 | 0.50 | | Bal | 1.00 | 5.00 | | 0.50 | | | | 水泵、水輪機部件 | | D 907 | 冷硬 | 0.20 | 21.00 | 1.00 | 2.50 | Bal | 3.00 | | 20.00 | 1.50 | | | | 熱剪刀片 | | Delcrome 90sc | 52 | 2.10 | 26.00 | 1.10 | | Bal | | | | 0.90 | | | | 挖掘設備、破碎輥、錘 | | Delcrome 91 | 55 | 3.00 | 31.00 | 0.60 | | Bal | 1.30 | | | 0.90 | | | | 破碎機輥、錘頭、泥漿泵部件 | | Delcrome 94 | 53 | 3.00 | 31.00 | 0.40 | | Bal | 1.30 | | | 0.90 | | | | 鏟斗齒、攪拌機、挖掘采礦設備 | | Delcrome 945 | 58 | 5.40 | 1.20 | | Bal | | | | 1.00 | | | Nb:5.00 | 耐侵蝕、抗高溫腐蝕及磨損場合 | | Delcrome 23 | 44 | 0.20 | 5.50 | 1.00 | &n, bsp;&, amp;, lt;, /TD> | Bal | 2.50 | V:7.0 | | 1.20 | | | | 低氫型焊條，用于鍛模、沖模 | Multipass235司太立焊條，Multipass235司太立焊條， ， ， ， 6)硫（s）硫是一種有害雜質，隨著硫含量的增加，將增大焊縫的熱裂紋傾向，因此焊芯中硫的含量不得大于0. 04%。在焊接重要結構時，硫含量不得大于0. 03%。， ， ， （3）藥皮類型：鈦鈣型 電源種類： 直流或交流 主要特點：藥皮中含氧化鈦30%以上，鈣、鎂的碳酸鹽20%以下，焊條工藝性能良好，熔渣流動性好，熔深一般，電弧穩(wěn)定，焊縫美觀，脫渣方便，適用于全位置焊接，如j422即屬此類型，是目前碳鋼焊條中使用最廣泛的一種焊條。， ， ， ， ， ， ， 焊條藥皮是指涂在焊芯表面的涂料層。藥皮在焊接過程中分解熔化后形成氣體和熔渣，起到機械保護、冶金處理、改善工藝性能的作用。藥皮的組成物有：礦物類（如大理石、氟石等）、鐵合金和金屬粉類（如錳鐵、鈦鐵等）、有機物類（如木粉、淀粉等）、化工產品類（如鈦***、水玻璃等）。焊條藥皮是決定焊縫質量的重要因素，在焊接過程中有以下幾方面的作用：， 焊條牌號的編制方法 ， | 電焊條 | 硬度 | 化學成分（重量%） | 典型用途 | | Electrode | A-91 | 60%碳化鎢、其余為鋼管、A-91中的91為碳化鎢顆粒硬度 | 風機攪拌機葉片、采礦、建筑易損件 | | 鑄棒 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | | Stellite 1 | 53 | 2.50 | 29.50 | 1.20 | 12.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 閥座、軸承、刀口等 | | Stellite 3 | 54 | 2.40 | 31.00 | 1.00 | 12.50 | 3.00 | | 3.00 | Bal | 1.00 | 針閥座、閥座、軋鋼導向輥 | | Stellite 4 | 48 | 0.90 | 32.00 | 1.00 | 13.50 | 1.00 | 0.50 | 0.50 | Bal | 0.50 | 熱壓模、熱擠壓模、干電池工業(yè) | | Stellite 6 | 43 | 1.20 | 29.00 | 1.20 | 4.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 發(fā)動機氣門、高溫高壓閥門、渦輪機葉片 | | Stellite 12 | 47 | 1.45 | 29.00 | 2.00 | 8.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 高溫高壓閥門、鋸齒、螺旋推桿等 | | Stellite 20 | 54 | 2.45 | 32.50 | 1.00 | 17.00 | 3.00 | 1.00 | 3.00 | Bal | 0.50 | 軸承套筒、耐磨板 | | Stellite 21 | 20 | 0.25 | 27.00 | 1.00 | 0.15 | 2.00 | 5.50 | 2.50 | Bal | 1.00 | 渦輪機葉片、各種液體閥、閥座、熱沖模等 | | Stellite 31 | 33 | 0.50 | 25.50 | 1.00 | 7.50 | 2.00 | 1.00 | 10.50 | Bal | 1.00 | 燃氣渦輪葉片 | | Stellite 190 | 58 | 3.20 | 26.00 | 1.00 | 14.00 | 5.00 | 1.00 | 3.00 | Bal | 1.00 | 石油鉆具 | | Stellite 706 | 42 | 1.20 | 30.00 | 1.20 | | 2.00 | 5.00 | 2.00 | Bal | 1.00 | 發(fā)動機氣門、高溫高壓閥門 | | Stellite 712 | 50 | 2.00 | 29.00 | 2.00 | | 2.00 | 8.50 | 2.00 | Bal | 2.00 | 高溫高壓閥門、螺旋推桿 | | Tribaloy 400 | 53 | 0.08 | 8.50 | 2.60 | | 1.50 | 28.50 | 1.50 | Bal | | 用于高溫強腐介質中的閘閥、擠塑器 | | Tribaloy 800 | 55 | 0.08 | 18.00 | 3.40 | | 1.50 | 28.50 | 1.50 | Bal | | 用于高溫強腐介質中的閘閥、擠塑器 | | Stellite F | 40 | 1.75 | 25.50 | 1.10 | | 1.15 | 0.60 | 22.50 | Bal | 0.30 | 內燃機進排氣閥 | Multipass235司太立焊條，Multipass235司太立焊條， ， 以結構鋼為例：牌號,編制法。結xxx,結為結構鋼焊條,第3個數(shù)字,代表藥皮類型,焊接電流要求,第1、2數(shù):代表焊縫金屬抗拉強度 。， 焊條就是涂有藥皮的供焊條電弧焊使用的熔化電極，它是由藥皮和焊芯兩部分組成的。在焊條前端藥皮有45°左右的倒角，這是為了便于引弧。在尾部有一段裸焊芯，約占焊條總長1/16，便于焊鉗夾持并有利于導電。焊條的直徑實際上是指焊芯直徑）通常為2、2.5、3.2或3、4、5或6mm等幾種規(guī)格，最常用的是小3.2、小4、小5三種，其長度“l(fā)”一般在200～550 mm之間。， ， （6）藥皮類型：高纖維素鉀型 ‖藥皮主要成分 ： 有機物15%以上，氧化鈦30%左右 ‖焊接電源：直流或交流， ， 1。(chh) 二個字母，中國航海產品代號。， ， （4）藥皮類型：氧化鐵型 ‖藥皮主要成分 ：多量氧化鐵及較多的錳鐵脫氧劑 ‖焊接電源： 直流或交流， ， （8）藥皮類型：低氫鉀型 ‖藥皮主要成分 ： 鈣、鎂的碳酸鹽和螢石 ‖焊接電源： 直流或交流， （9）藥皮類型：鹽基型 電源種類：直流 主要特點： 藥皮中含多量氯化物和氟化物，主要用于鋁及鋁合金焊條。吸潮性強，焊前要烘干。藥皮熔點低，熔化速度快。采用直流電源，焊接工藝性較差，短弧操作，熔渣有腐蝕性，焊后需用熱水清洗。， ， ， 5)鎳(ni）鎳對鋼的韌性有比較顯著的效果，一般低溫沖擊值要求較高時，適當摻入一些鎳。，
| 鑄棒 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | B | | Deloro 40 | 40 | 0.30 | 7.50 | 3.50 | | 2.20 | 0.10 | Bal | | 0.10 | 1.70 | 螺旋送料器、模芯、核工業(yè)中閥門的密封面 | | Deloro 45 | 45 | 0.37 | 8.75 | 3.80 | | 4.00 | 0.10 | Bal | | 0.10 | 2.00 | 排氣閥密封面、柱塞 | | Deloro 50 | 50 | 0.45 | 11.25 | 4.00 | | 2.80 | 0.10 | Bal | | 0.10 | 2.20 | 泵軸、紙漿刀、閥門、密封環(huán)、軸套 | | Deloro 55 | 55 | 0.50 | 11.00 | 3.60 | | 4.50 | 0.10 | Bal | | 0.50 | 2.10 | 閥門、密封環(huán)、軸套 | | Deloro 60 | 59 | 0.65 | 15.00 | 4.30 | | 4.00 | 0.10 | Bal | | 0.10 | 3.10 | 擠壓模、螺旋筒體、泵葉、柱塞 | | Deloro 6325 | 56 | 0.50 | 16.00 | 4.00 | | 4.50 | 3.00 | Bal | | 0.10 | 3.50 | 耐蝕泵、軸、軸套 | | Tribaloy 700 | 54 | 0.08 | 15.50 | 3.40 | | 1.50 | 32.50 | Bal | 1.50 | | | 核工業(yè)應用抗蝕抗氧化抗輻射 | | Nistelle B | 冷硬 | 0.10 | 1.00 | 1.00 | | 5.00 | 28.00 | Bal | 2.50 | 1.00 | | 高溫耐蝕密封環(huán) | Multipass235司太立焊條， ， 2)錳(mn)錳在鋼中是一種較好的合金劑，隨著錳含量的增加，其強度和韌性會有所提高。在焊接過程中，錳也是一種較好的脫氧劑，能減少焊縫中氧的含量。錳與硫化合形成硫化錳浮于熔渣中，從而減少焊縫熱裂紋傾向。因此一般碳素結構鋼焊芯的含錳量為0. 30%～0. 55%，焊接某些特殊用途的鋼絲，其含錳量高達1 ．70%一2. 10%。， 三、保證焊縫脫氧、去硫磷雜質。焊接過程中雖然進行了保護，但仍難免有少量氧進入熔池，使金屬及合金元素氧化，燒損合金元素，降低焊縫質量。因此，需要在焊條藥皮中加入還原劑(如錳、硅、鈦、鋁等)，使已進入熔池的氧化物還原。http://www.wanhonghanjie.com， （7）藥皮類型：低氫鈉型 ‖藥皮主要成分 ：鈣、鎂的碳酸鹽和螢石 ‖焊接電源：直流， ， ， ， 三、保證焊縫脫氧、去硫磷雜質。焊接過程中雖然進行了保護，但仍難免有少量氧進入熔池，使金屬及合金元素氧化，燒損合金元素，降低焊縫質量。因此，需要在焊條藥皮中加入還原劑(如錳、硅、鈦、鋁等)，使已進入熔池的氧化物還原。http://www.wanhonghanjie.com， （4）藥皮類型：鈦鐵礦型 電源種類： 直流或交流 主要特點：藥皮中含鈦鐵礦305，焊條熔化速度快，熔渣流動性好，熔深較深，脫渣容易，焊波整齊，電弧穩(wěn)定，平焊、平角焊工藝性能較好，立焊稍次，焊縫有較好的抗裂性。， 3)硅(si )硅也是一種較好的合金劑，在鋼中加入適量的硅能提高鋼的屈服強度、彈性及抗酸性能；若含量過高，則降低塑性和韌性。在焊接過程中，硅也具有較好的脫氧能力，與氧形成二氧化硅，但它會提高渣的粘度，易促進非金屬夾雜物生成。， ， 1)碳(c)碳是鋼中的主要合金元素，當含碳量增加時，鋼的強度、硬度明顯提高，而塑性降低。在焊接過程中，碳起到一定的脫氧作用，在電弧高溫作用下與氧發(fā)生化合作用，生成一氧化碳和二氧化碳氣體，將電弧區(qū)和熔池周圍空氣排除，防止空氣中的氧、氮有害氣體對熔池產生的不良影響，減少焊縫金屬中氧和氮的含量。若含碳量過高，還原作用劇烈，會引起較大的飛濺和氣孔。考慮到碳對鋼的淬硬性及其對裂紋敏感性增加的影響，低碳鋼焊芯的含碳量一般為0. 1%。， ， ， ， 焊條 - 藥皮， ， ， ， ， 焊條藥皮是指涂在焊芯表面的涂料層。藥皮在焊接過程中分解熔化后形成氣體和熔渣，起到機械保護、冶金處理、改善工藝性能的作用。藥皮的組成物有：礦物類（如大理石、氟石等）、鐵合金和金屬粉類（如錳鐵、鈦鐵等）、有機物類（如木粉、淀粉等）、化工產品類（如鈦***、水玻璃等）。焊條藥皮是決定焊縫質量的重要因素，在焊接過程中有以下幾方面的作用：， (1)容易引弧，保證電弧穩(wěn)定，在焊接過程中飛濺小。， 四、為焊縫補充合金元素。由于電弧的高溫作用，焊縫金屬的合金元素會被蒸發(fā)燒損，使焊縫的機械性能降低。因此，必須通過藥皮向焊縫加入適當?shù)暮辖鹪兀詮浹a合金元素的燒損，保證或提高焊縫的機械性能。對有些合金鋼的焊接，也需要通過藥皮向焊縫滲入合金，使焊縫金屬能與母材金屬成分相接近，機械性能趕上甚至超過基本金屬。， （8）藥皮類型：低氫鉀型 ‖藥皮主要成分 ： 鈣、鎂的碳酸鹽和螢石 ‖焊接電源： 直流或交流， ， | 
