| 管狀焊絲 | 焊劑 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | Mo | Mn | Fe | W | Ni | V | B | 其他 | | Delcrome 103 | 107 | 54 | 5.15 | 27.50 | 1.50 | | 2.50 | Bal | | | | | | 磨煤輥 | | Multipass 104 | 431 | 28 | 0.25 | 1.20 | 1.50 | | 3.00 | Bal | | | | | | 軋輥等堆焊過渡層及軸的修復 | | Multipass 105 | 431 | 45 | 0.50 | 4.00 | 1.10 | 0.50 | 2.75 | Bal | | | | | | 拖拉機惰輪、礦車輪、導輥 | | Multipass 107 | 431 | 37 | 0.35 | 2.70 | 1.20 | 0.25 | 2.70 | Bal | | | | | | 卷筒、拖拉機惰輪、礦車輪 | | Multipass 109 | 260 | | 0.45 | 3.10 | 0.60 | | 0.60 | Bal | | 0.5 | | | | 管模、鋁軋輥等 | | Multipass 224 | 107 | 46 | 0.45 | 5.50 | 0.65 | 1.10 | 1.80 | Bal | 1.50 | | | | | 各類軋輥及連鑄第3區輥 | | Multipass 224H | 107 | 53 | 0.55 | 6.50 | 0.65 | 1.10 | 1.80 | Bal | 1.50 | | | | 1.0 | 熱軋工作輥、支撐輥、開坯輥 | | Multipass 224HC | 107 | 58 | 0.75 | 7.70 | 0.75 | 1.80 | 1.70 | Bal | 2.60 | | | | 1.0 | 支撐輥、校直輥、助卷輥 | | Multipass 225 | 107 | 59 | 0.90 | 6.00 | 0.50 | 1.20 | 0.80 | Bal | 8.60 | | | | | 熱軋支撐輥 | | Multipass 235 | 107 | 60 | 0.45 | 9.00 | | 2.20 | 0.70 | Bal | 8.40 | Co:10.5 | 0.30 | | | 熱軋支撐輥 | | Multipass 236 | | | 0.28 | 3.10 | 0.70 | 2.00 | 0.70 | Bal | 1.90 | | 0.65 | | | 鋼管成型輥 | | Multipass 915 | 107 | 60 | 1.20 | 20.00 | 0.50 | | 0.70 | Bal | | | | 4.00 | | 高速磨打擊板等耐強沖擊，強磨粒磨損場合 | | Delstain 414-S | 260 | 40 | 0.20 | 14.00 | 0.50 | 1.00 | 1.40 | Bal | | 4.20 | | | | 連鑄輥等耐磨耐高溫場合 | | Delstain 420 | 260 | 46 | 0.40 | 13.00 | 0.50 | | 1.40 | Bal | | | | | | 一般軋鋼輥、剎車鼓、卷輥 | | Delstain 423 | 107 | 45 | 0.33 | 13.50 | 0.50 | 1.20 | 1.50 | Bal | | 2.50 | 0.20 | | | 連鑄機輥、熱軋輥堆焊 | | Delstain 424H | 260 | 49 | 0.40 | 12.00 | 0.50 | 0.90 | 2.20 | Bal | | 1.40 | | | | 有色工作輥的堆焊 | | Delstain 430 | 260 | | 0.10 | 19.00 | 0.50 | | 0.70 | Bal | | 0.60 | | | | 連鑄輥等耐磨耐高溫場合 | | Delcrome 911 | 107 | 57 | 6.60 | 36.50 | 0.40 | | 0.40 | Bal | | | | | | 磨煤輥堆焊 | | Delcrome 100HD | 107 | 57 | 6.80 | 29.00 | 1.00 | | 2.0 | Bal | | | | | Zr:0.45 | 磨煤輥等耐中等沖擊，強磨粒磨損場合 | | STW 101 | 431 | HB:250 | 0.25 | 1.35 | 0.55 | 0.60 | 1.35 | Bal | | | 0.25 | | | 碳鋼、低合金鋼部件修復 | | STW 102 | 431 | 36 | 0.25 | 2.95 | 0.55 | 1.00 | 1.00 | Bal | | 1.35 | 0.10 | | | 碳鋼、低合金鋼部件修復 | | STW 103 | | | 0.35 | 3.00 | 0.70 | 2.00 | 1.40 | Bal | | | 0.60 | | | 碳鋼、低合金鋼部件修復 | StelliteF堆焊焊條，StelliteF堆焊焊條， ， ， ， 焊芯是根據國家標準“焊接用鋼絲”（gb 1300-77)的規定分類的，用于焊接的專用鋼絲可分為碳素結構鋼、合金結構鋼、不銹鋼三類。， ， 5。(crni)1～2字母，附加合金元素或焊條特性。， 2.焊條種類：（見表1） ， ， ， （5）藥皮類型：氧化鐵型 電源種類： 直流或交流 主要特點：藥皮中含多量氧化鐵和較多的錳鐵脫氧劑，熔深大，熔化速度快，焊接生產率較高，電弧穩定，再引弧方便，立焊、仰焊較困難，飛濺稍大，焊縫抗熱裂性能較好，適用于中厚板焊接。由于電弧吹力大，適于野外操作。若藥皮中加入一定量的鐵粉，為鐵粉氧化鈦型。， ， ， （8）藥皮類型：石墨型 電源種類：直流或交流 主要特點：藥皮中含有多量石墨，通常用于鑄鐵或堆焊焊條。采用低碳鋼焊芯時，焊接工藝性能較差，飛濺較多，煙霧較大，熔渣少，適于平焊。采用有色金屬焊芯時，能改善其工藝性能，但電流不易過大。， ， ， | 管狀焊絲 | 硬度 | 化學成分（重量%） | 典型用途 | | Tungsmooth 60 | A-91 | 60%碳化鎢、其余為鋼管、A-91中的91為碳化鎢顆粒硬度 | 風機攪拌機葉片、采礦、建筑易損件 |
| 管狀焊絲 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | Mo | Mn | Fe | Ni | Al | 其他 | | Delcrome 11-o | 50 | 3.20 | 14.50 | 0.90 | 0.45 | 1.40 | Bal | | | | 破碎機錘頭、挖土機齒 | | Delcrome 94-o | 57 | 3.20 | 24.50 | 0.70 | | 0.80 | Bal | 2.80 | | | 筑路機零件、攪拌葉片 | | Delcrome 100-o | 57 | 3.80 | 26.50 | 1.40 | 1.30 | 1.90 | Bal | | | | 磨煤輥 | | Delcrome 100HC-o | 60 | 5.50 | 26.50 | 2.40 | 1.30 | 1.90 | Bal | | | | 磨煤輥、破碎輥 | | Delcrome 117-o | 43 | 2.30 | 10.50 | 1.30 | 1.50 | 1.50 | Bal | zr:0.40 | | Cu:0.40 | 破碎輥、錘頭 | | Delcrome 150-o | 58 | 2.20 | 7.00 | | 2.00 | 1.00 | Bal | V:0.20 | | Ti:7.00 | 水泥擠壓輥、錘頭、農具 | | Delcrome 945-o | 57 | 5.00 | 21.50 | 0.70 | 4.50 | 0.70 | Bal | W:2.00 | | Nb:7.00 | 高爐加料槽板、閘閥 | | Build up | 35 | 0.15 | 0.90 | 0.90 | 0.40 | 1.80 | Bal | | | | 碳鋼、低合金鋼恢復尺寸如齒輪、錘頭 | | Ni-Mang-o | 冷硬 | 0.85 | 3.00 | 0.50 | | 14.00 | Bal | 3.00 | | | 破碎機輥、顎板、挖泥機刀片 | | Sta-Mang-o | 冷硬 | 0.10 | 10.00 | 0.50 | 0.80 | 15.50 | Bal | 0.85 | | | 破碎機、鐵鏟、鐵路道岔 | | Multipass 4-o | 34 | 0.15 | 0.70 | 1.10 | 0.30 | 2.00 | Bal | | | | 碳鋼、低合金鋼部件修復 | | Multipass 5-o | 44 | 0.10 | 2.30 | 0.30 | 0.50 | 1.40 | Bal | | | | 拖拉機惰輪、起重機輪 | | Multipass 1265-g | 55 | 0.65 | 5.50 | 0.50 | 1.50 | 1.00 | Bal | W:1.50 | | V:0.30 | 冷沖壓模 | | Delcrome 90G | 48 | 2.40 | 24.00 | 0.60 | | 0.90 | Bal | | | | 鏟斗齒、排氣葉、提升斗 | | Delcrome 94G | 52 | 3.00 | 28.00 | 1.40 | | 1.20 | Bal | B:0.80 | | | 鏟斗齒、攪拌機、破碎輥 | | Mulitpass 106 | | 0.10 | | 0.90 | 5.20 | 1.40 | Bal | 5.20 | | | 管模，鋁軋輥等 | | Delcrome 165 | 62 | 6.80 | 30.00 | 3.00 | 0.50 | 0.50 | Bal | W:4.20 | | Nb:2.60 | 磨煤 輥等耐中等沖擊，強磨粒磨損場合 | | Delstain 414N-o | 47 | 0.20 | 14.00 | 0.50 | 1.00 | 1.30 | Bal | 4.20 | | N:0.22 | 連鑄輥等耐磨耐高溫場合 | | Delstain 431 | 33 | 0.40 | 17.50 | 0.50 | | 1.20 | Bal | | | | 連鑄輥等耐磨耐高溫場合 | | Delcrome 103HD | 60 | 5.60 | 30.00 | 1.10 | 0.80 | 1.20 | Bal | | | Cu:0.10 | 磨煤輥等 | | Stellarc 420 | 430（HV） | 0.3 | 13 | 1 | | 1 | Bal | | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 430 | 400（HV） | 0.7 | 17 | 1 | 0.5 | 1 | Bal | | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 316 | 240（HV） | 0.08 | 18 | 0.7 | 2.5 | 1 | Bal | 13 | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 100 | 660（HV） | 5 | 28 | 0.5 | | 1 | Bal | | | | 具有優良的耐磨性 | | Stellarc 250 | | | 1 | 0.5 | 0.5 | 1 | Bal | | | WC:50 | 風機、風管、煙道內壁 | | Stellarc 45 | 400（HV） | | 45 | | | | | Bal | | | 風機、風管、煙道內壁 | | Stellarc 95 | 480（HV） | | | | | | | Bal | 5 | | 打底涂層 | | Stellarc 625 | 260（HV） | 0.08 | 21 | | 9 | | 5 | Bal | 5 | Nb+Ta:4 | 優異的抗高溫腐蝕及耐磨介質 | | Stellarc 276 | | 0.08 | 16 | | 16 | | 5 | Bal | | W:4 | 耐腐蝕性能優異，能抗硫酸、鹽酸或其他有機酸的腐蝕 | StelliteF堆焊焊條，StelliteF堆焊焊條， （7）藥皮類型：低氫鉀型 （低氫鈉型） 電源種類：直流或交流 （直流） 主要特點：藥皮成分以碳酸鹽和螢石為主。焊條使用前須經300～400℃烘焙。短弧操作，焊接工藝性一般，可全位置焊接。焊縫有良好的抗裂性和綜合力學性力。適于焊接重要的焊接結構。按照藥皮中穩弧劑量、鐵粉量和黏結劑不同，分為低氫鈉型、低氫鉀型和鐵粉低氫型等http://www.wanhonghanjie.com， ， ， ， 以結構鋼為例：牌號,編制法。結xxx,結為結構鋼焊條,第3個數字,代表藥皮類型,焊接電流要求,第1、2數:代表焊縫金屬抗拉強度 。， 焊條中被藥皮包覆的金屬芯稱為焊芯。焊芯一般是一根具有一定長度及直徑的鋼絲。焊接時，焊芯有兩個作用：一是傳導焊接電流，產生電弧把電能轉換成熱能，二是焊芯本身熔化作為填充金屬與液體母材金屬熔合形成焊縫。， ， ， ， ， 焊條藥皮類型分類 ， ， 3。(50)二個數字，熔敷金屬強度或合金類型。， 1.chh：中國航海產品代號http://www.wanhonghanjie.com， ， | 電焊條 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | B | Cu | 其他 | | Stellite 1 | 48 | 2.20 | 29.00 | 2.00 | 14.00 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 閥座、軸承、刀口等 | | Stellite 6 | 40 | 1.00 | 29.00 | 1.00 | 4.50 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 發動機氣門、高溫高壓閥門、渦輪機葉片 | | Stellite 12 | 44 | 1.30 | 29.00 | 1.00 | 9.00 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 高溫高壓閥門、鋸齒、螺旋推桿等 | | Stellite 21 | 23 | 0.30 | 28.00 | 1.00 | | 2.50 | 5.50 | 2.50 | Bal | 2.00 | | | | 渦輪機葉片、閥座、熱沖模 | | Stellite 25 | 冷硬 | 0.15 | 20.00 | 1.00 | 14.00 | 3.00 | 0.50 | 10.00 | Bal | 1.50 | | | | 高溫耐蝕密封面、擠壓模 | | Nistelle C | | 0.10 | 17.00 | | 5.00 | 6.00 | 17.00 | Bal | | | | | | 高溫耐蝕密封環 | | Ni-Mang | 冷硬 | 0.60 | 2.70 | 0.20 | | Bal | | 3.70 | | 13.50 | | | | 錘式破碎機、高錳鋼部件焊接 | | STE 308-16 | | 0.08 | 19.50 | 0.90 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | | 用于焊接Cr18Ni8不銹鋼 | | STE 308L-16 | | 0.03 | 19.50 | 0.90 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | | 用于焊接超低碳Cr18Ni8不銹鋼 | | STE 309-16 | | 0.15 | 23.50 | 0.90 | | Bal | 0.50 | 13.00 | | 0.80 | | 0.50 | | 用于焊接Cr22Nil2不銹鋼及用于不銹鋼與低碳鋼或低合金鋼之間的焊接 | | STE 309L-16 | | 0.02 | 23.50 | 0.90 | | Bal | 0.50 | 13.00 | | 0.80 | | 0.50 | | 打底層焊接，異種鋼焊接，易產生裂紋部位的焊接 | | STE 309Mo-16 | | 0.12 | 23.50 | 0.90 | | Bal | 2.50 | 13.00 | | 0.80 | | | | 用于焊接Cr22Nil2-Mo不銹鋼 | | STE 309MoL-16 | | 0.03 | 23.50 | 0.90 | | Bal | 2.50 | 13.00 | | 0.80 | | | | 用于焊接超低碳Cr22Nil2Mo不銹鋼 | | STE 310-16 | | 0.20 | 26.50 | 0.75 | | Bal | 0.50 | 21.50 | | 1.50 | | 0.50 | | 用于焊接Cr25Ni20不銹鋼 | | STE 310Mo-16 | | 0.08 | 26.50 | 0.75 | | Bal | 2.50 | 21.00 | | 1.20 | | 0.50 | | 耐硫酸腐蝕、抗裂性、高溫性能優良 | | STE 316-16 | | 0.05 | 18.50 | 0.90 | | Bal | 2.50 | 12.50 | | 0.80 | | 0.50 | | 用于焊接Cr18Ni12Mo2不銹鋼 | | STE 316L-16 | | 0.03 | 18.50 | 0.90 | | Bal | 2.50 | 12.50 | | 0.80 | | 0.50 | | 用于焊接超低碳Cr18Ni12Mo2不銹鋼 | | STE 316LF | | 0.02 | 18.00 | 0.75 | | Bal | 2.70 | 16.00 | | 2.00 | | 0.50 | | 耐尿素腐蝕性優良 | | STE 347-16 | | 0.08 | 19.50 | 0.50 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | 8xc-1.00 | 用于焊接Cr18Ni8含鈮或鈦的不銹鋼 | | STE 997 | 56 | 0.60 | 5.50 | 0.80 | | Bal | 4.00 | W:7.0 | | 0.70 | | | | 低氫型高速鋼焊條 | | D 287 | 40 | 0.10 | 14.00 | 0.50 | | Bal | 1.00 | 5.00 | | 0.50 | | | | 水泵、水輪機部件 | | D 907 | 冷硬 | 0.20 | 21.00 | 1.00 | 2.50 | Bal | 3.00 | | 20.00 | 1.50 | | | | 熱剪刀片 | | Delcrome 90sc | 52 | 2.10 | 26.00 | 1.10 | | Bal | | | | 0.90 | | | | 挖掘設備、破碎輥、錘 | | Delcrome 91 | 55 | 3.00 | 31.00 | 0.60 | | Bal | 1.30 | | | 0.90 | | | | 破碎機輥、錘頭、泥漿泵部件 | | Delcrome 94 | 53 | 3.00 | 31.00 | 0.40 | | Bal | 1.30 | | | 0.90 | | | | 鏟斗齒、攪拌機、挖掘采礦設備 | | Delcrome 945 | 58 | 5.40 | 1.20 | | Bal | | | | 1.00 | | | Nb:5.00 | 耐侵蝕、抗高溫腐蝕及磨損場合 | | Delcrome 23 | 44 | 0.20 | 5.50 | 1.00 | &n, bsp;&, amp;, lt;, /TD> | Bal | 2.50 | V:7.0 | | 1.20 | | | | 低氫型焊條，用于鍛模、沖模 | StelliteF堆焊焊條，StelliteF堆焊焊條， ， ， ， 三、保證焊縫脫氧、去硫磷雜質。焊接過程中雖然進行了保護，但仍難免有少量氧進入熔池，使金屬及合金元素氧化，燒損合金元素，降低焊縫質量。因此，需要在焊條藥皮中加入還原劑(如錳、硅、鈦、鋁等)，使已進入熔池的氧化物還原。http://www.wanhonghanjie.com， 6。(fe13)字母+二個數字，焊條名義效率。， ， ， 2.焊條種類：（見表1） ， ， (3)熔渣的比重應小于熔化金屬的比重，凝固溫度也應稍低于金屬凝固溫度，渣殼應易脫掉；， 4。(7)一個數字，藥皮類型及電流種類。， ， ， ， ， | 電焊條 | 硬度 | 化學成分（重量%） | 典型用途 | | Electrode | A-91 | 60%碳化鎢、其余為鋼管、A-91中的91為碳化鎢顆粒硬度 | 風機攪拌機葉片、采礦、建筑易損件 | | 鑄棒 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | | Stellite 1 | 53 | 2.50 | 29.50 | 1.20 | 12.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 閥座、軸承、刀口等 | | Stellite 3 | 54 | 2.40 | 31.00 | 1.00 | 12.50 | 3.00 | | 3.00 | Bal | 1.00 | 針閥座、閥座、軋鋼導向輥 | | Stellite 4 | 48 | 0.90 | 32.00 | 1.00 | 13.50 | 1.00 | 0.50 | 0.50 | Bal | 0.50 | 熱壓模、熱擠壓模、干電池工業 | | Stellite 6 | 43 | 1.20 | 29.00 | 1.20 | 4.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 發動機氣門、高溫高壓閥門、渦輪機葉片 | | Stellite 12 | 47 | 1.45 | 29.00 | 2.00 | 8.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 高溫高壓閥門、鋸齒、螺旋推桿等 | | Stellite 20 | 54 | 2.45 | 32.50 | 1.00 | 17.00 | 3.00 | 1.00 | 3.00 | Bal | 0.50 | 軸承套筒、耐磨板 | | Stellite 21 | 20 | 0.25 | 27.00 | 1.00 | 0.15 | 2.00 | 5.50 | 2.50 | Bal | 1.00 | 渦輪機葉片、各種液體閥、閥座、熱沖模等 | | Stellite 31 | 33 | 0.50 | 25.50 | 1.00 | 7.50 | 2.00 | 1.00 | 10.50 | Bal | 1.00 | 燃氣渦輪葉片 | | Stellite 190 | 58 | 3.20 | 26.00 | 1.00 | 14.00 | 5.00 | 1.00 | 3.00 | Bal | 1.00 | 石油鉆具 | | Stellite 706 | 42 | 1.20 | 30.00 | 1.20 | | 2.00 | 5.00 | 2.00 | Bal | 1.00 | 發動機氣門、高溫高壓閥門 | | Stellite 712 | 50 | 2.00 | 29.00 | 2.00 | | 2.00 | 8.50 | 2.00 | Bal | 2.00 | 高溫高壓閥門、螺旋推桿 | | Tribaloy 400 | 53 | 0.08 | 8.50 | 2.60 | | 1.50 | 28.50 | 1.50 | Bal | | 用于高溫強腐介質中的閘閥、擠塑器 | | Tribaloy 800 | 55 | 0.08 | 18.00 | 3.40 | | 1.50 | 28.50 | 1.50 | Bal | | 用于高溫強腐介質中的閘閥、擠塑器 | | Stellite F | 40 | 1.75 | 25.50 | 1.10 | | 1.15 | 0.60 | 22.50 | Bal | 0.30 | 內燃機進排氣閥 | StelliteF堆焊焊條，StelliteF堆焊焊條， ， ， (1)容易引弧，保證電弧穩定，在焊接過程中飛濺小。， ， ， ， ， （1）藥皮類型：不屬已規定的類型 電源種類：不規定 主要特點：在某些焊條中采用氧化鋯、金紅石堿性型等，這些新渣系目前尚未形成系列， 人們在實踐過程中發現如果在光焊條外面涂一層由各種礦物等組成的藥皮，能使電弧燃燒穩定，焊縫質量得到提高，這種焊條叫藥皮焊條。隨著工業技術的不斷發展，人們創制出了廣泛應用的優質厚藥皮焊條。http://www.wanhonghanjie.com， （3）藥皮類型：鈦鈣型 電源種類： 直流或交流 主要特點：藥皮中含氧化鈦30%以上，鈣、鎂的碳酸鹽20%以下，焊條工藝性能良好，熔渣流動性好，熔深一般，電弧穩定，焊縫美觀，脫渣方便，適用于全位置焊接，如j422即屬此類型，是目前碳鋼焊條中使用最廣泛的一種焊條。， ， 4)鉻(cr）鉻能夠提高鋼的硬度、耐磨性和耐腐蝕性。對于低碳鋼來說，鉻便是一種偶然的雜質。鉻的主要冶金特征是易于急劇氧化，形成難熔的氧化物三氧化二鉻(cr203)，從而增加了焊縫金屬夾雜物的可能性。三氧化二鉻過渡到熔渣后，能使熔渣粘度提高，流動性降低。， ， ， ，
| 鑄棒 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | B | | Deloro 40 | 40 | 0.30 | 7.50 | 3.50 | | 2.20 | 0.10 | Bal | | 0.10 | 1.70 | 螺旋送料器、模芯、核工業中閥門的密封面 | | Deloro 45 | 45 | 0.37 | 8.75 | 3.80 | | 4.00 | 0.10 | Bal | | 0.10 | 2.00 | 排氣閥密封面、柱塞 | | Deloro 50 | 50 | 0.45 | 11.25 | 4.00 | | 2.80 | 0.10 | Bal | | 0.10 | 2.20 | 泵軸、紙漿刀、閥門、密封環、軸套 | | Deloro 55 | 55 | 0.50 | 11.00 | 3.60 | | 4.50 | 0.10 | Bal | | 0.50 | 2.10 | 閥門、密封環、軸套 | | Deloro 60 | 59 | 0.65 | 15.00 | 4.30 | | 4.00 | 0.10 | Bal | | 0.10 | 3.10 | 擠壓模、螺旋筒體、泵葉、柱塞 | | Deloro 6325 | 56 | 0.50 | 16.00 | 4.00 | | 4.50 | 3.00 | Bal | | 0.10 | 3.50 | 耐蝕泵、軸、軸套 | | Tribaloy 700 | 54 | 0.08 | 15.50 | 3.40 | | 1.50 | 32.50 | Bal | 1.50 | | | 核工業應用抗蝕抗氧化抗輻射 | | Nistelle B | 冷硬 | 0.10 | 1.00 | 1.00 | | 5.00 | 28.00 | Bal | 2.50 | 1.00 | | 高溫耐蝕密封環 | StelliteF堆焊焊條， （3）藥皮類型：鈦鈣型 電源種類： 直流或交流 主要特點：藥皮中含氧化鈦30%以上，鈣、鎂的碳酸鹽20%以下，焊條工藝性能良好，熔渣流動性好，熔深一般，電弧穩定，焊縫美觀，脫渣方便，適用于全位置焊接，如j422即屬此類型，是目前碳鋼焊條中使用最廣泛的一種焊條。， ， 一個焊條牌號由六部份組成。例如chhe507crnife13可分割為：，， 二、保護焊接熔池。焊接過程中，空氣中的氧、氮及水蒸氣浸入焊縫，會給焊縫帶來不利的影響。不僅形成氣孔，而且還會降低焊縫的機械性能，甚至導致裂紋。而焊條藥皮熔化后，產生的大量氣體籠罩著電弧和熔池，會減少熔化的金屬和空氣的相互作用。焊縫冷卻時，熔化后的藥皮形成一層熔渣，覆蓋在焊縫表面，保護焊縫金屬并使之緩慢冷卻、減少產生氣孔的可能性。， ， ， ， 此外，對于藥皮中含有多量鐵粉的焊條，可以稱為鐵粉焊條。這時，按照相應焊條藥皮的主要成分，又可分為鐵粉鈦型、鐵粉鈦鐵礦型、鐵粉氧化鐵型、鐵粉低氫型等，構成了鐵粉焊條系列。， ， ， 6)硫（s）硫是一種有害雜質，隨著硫含量的增加，將增大焊縫的熱裂紋傾向，因此焊芯中硫的含量不得大于0. 04%。在焊接重要結構時，硫含量不得大于0. 03%。， ， （10）藥皮類型：石墨型 ‖藥皮主要成分 ：多量石墨 ‖ 焊接電源：直流或交流， ， （船用焊條除外）， ， 四、為焊縫補充合金元素。由于電弧的高溫作用，焊縫金屬的合金元素會被蒸發燒損，使焊縫的機械性能降低。因此，必須通過藥皮向焊縫加入適當的合金元素，以彌補合金元素的燒損，保證或提高焊縫的機械性能。對有些合金鋼的焊接，也需要通過藥皮向焊縫滲入合金，使焊縫金屬能與母材金屬成分相接近，機械性能趕上甚至超過基本金屬。， ， ， （5）藥皮類型：氧化鐵型 電源種類： 直流或交流 主要特點：藥皮中含多量氧化鐵和較多的錳鐵脫氧劑，熔深大，熔化速度快，焊接生產率較高，電弧穩定，再引弧方便，立焊、仰焊較困難，飛濺稍大，焊縫抗熱裂性能較好，適用于中厚板焊接。由于電弧吹力大，適于野外操作。若藥皮中加入一定量的鐵粉，為鐵粉氧化鈦型。， 4)鉻(cr）鉻能夠提高鋼的硬度、耐磨性和耐腐蝕性。對于低碳鋼來說，鉻便是一種偶然的雜質。鉻的主要冶金特征是易于急劇氧化，形成難熔的氧化物三氧化二鉻(cr203)，從而增加了焊縫金屬夾雜物的可能性。三氧化二鉻過渡到熔渣后，能使熔渣粘度提高，流動性降低。， ， 2)錳(mn)錳在鋼中是一種較好的合金劑，隨著錳含量的增加，其強度和韌性會有所提高。在焊接過程中，錳也是一種較好的脫氧劑，能減少焊縫中氧的含量。錳與硫化合形成硫化錳浮于熔渣中，從而減少焊縫熱裂紋傾向。因此一般碳素結構鋼焊芯的含錳量為0. 30%～0. 55%，焊接某些特殊用途的鋼絲，其含錳量高達1 ．70%一2. 10%。， ， | 