| 管狀焊絲 | 焊劑 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | Mo | Mn | Fe | W | Ni | V | B | 其他 | | Delcrome 103 | 107 | 54 | 5.15 | 27.50 | 1.50 | | 2.50 | Bal | | | | | | 磨煤輥 | | Multipass 104 | 431 | 28 | 0.25 | 1.20 | 1.50 | | 3.00 | Bal | | | | | | 軋輥等堆焊過渡層及軸的修復 | | Multipass 105 | 431 | 45 | 0.50 | 4.00 | 1.10 | 0.50 | 2.75 | Bal | | | | | | 拖拉機惰輪、礦車輪、導輥 | | Multipass 107 | 431 | 37 | 0.35 | 2.70 | 1.20 | 0.25 | 2.70 | Bal | | | | | | 卷筒、拖拉機惰輪、礦車輪 | | Multipass 109 | 260 | | 0.45 | 3.10 | 0.60 | | 0.60 | Bal | | 0.5 | | | | 管模、鋁軋輥等 | | Multipass 224 | 107 | 46 | 0.45 | 5.50 | 0.65 | 1.10 | 1.80 | Bal | 1.50 | | | | | 各類軋輥及連鑄第3區輥 | | Multipass 224H | 107 | 53 | 0.55 | 6.50 | 0.65 | 1.10 | 1.80 | Bal | 1.50 | | | | 1.0 | 熱軋工作輥、支撐輥、開坯輥 | | Multipass 224HC | 107 | 58 | 0.75 | 7.70 | 0.75 | 1.80 | 1.70 | Bal | 2.60 | | | | 1.0 | 支撐輥、校直輥、助卷輥 | | Multipass 225 | 107 | 59 | 0.90 | 6.00 | 0.50 | 1.20 | 0.80 | Bal | 8.60 | | | | | 熱軋支撐輥 | | Multipass 235 | 107 | 60 | 0.45 | 9.00 | | 2.20 | 0.70 | Bal | 8.40 | Co:10.5 | 0.30 | | | 熱軋支撐輥 | | Multipass 236 | | | 0.28 | 3.10 | 0.70 | 2.00 | 0.70 | Bal | 1.90 | | 0.65 | | | 鋼管成型輥 | | Multipass 915 | 107 | 60 | 1.20 | 20.00 | 0.50 | | 0.70 | Bal | | | | 4.00 | | 高速磨打擊板等耐強沖擊，強磨粒磨損場合 | | Delstain 414-S | 260 | 40 | 0.20 | 14.00 | 0.50 | 1.00 | 1.40 | Bal | | 4.20 | | | | 連鑄輥等耐磨耐高溫場合 | | Delstain 420 | 260 | 46 | 0.40 | 13.00 | 0.50 | | 1.40 | Bal | | | | | | 一般軋鋼輥、剎車鼓、卷輥 | | Delstain 423 | 107 | 45 | 0.33 | 13.50 | 0.50 | 1.20 | 1.50 | Bal | | 2.50 | 0.20 | | | 連鑄機輥、熱軋輥堆焊 | | Delstain 424H | 260 | 49 | 0.40 | 12.00 | 0.50 | 0.90 | 2.20 | Bal | | 1.40 | | | | 有色工作輥的堆焊 | | Delstain 430 | 260 | | 0.10 | 19.00 | 0.50 | | 0.70 | Bal | | 0.60 | | | | 連鑄輥等耐磨耐高溫場合 | | Delcrome 911 | 107 | 57 | 6.60 | 36.50 | 0.40 | | 0.40 | Bal | | | | | | 磨煤輥堆焊 | | Delcrome 100HD | 107 | 57 | 6.80 | 29.00 | 1.00 | | 2.0 | Bal | | | | | Zr:0.45 | 磨煤輥等耐中等沖擊，強磨粒磨損場合 | | STW 101 | 431 | HB:250 | 0.25 | 1.35 | 0.55 | 0.60 | 1.35 | Bal | | | 0.25 | | | 碳鋼、低合金鋼部件修復 | | STW 102 | 431 | 36 | 0.25 | 2.95 | 0.55 | 1.00 | 1.00 | Bal | | 1.35 | 0.10 | | | 碳鋼、低合金鋼部件修復 | | STW 103 | | | 0.35 | 3.00 | 0.70 | 2.00 | 1.40 | Bal | | | 0.60 | | | 碳鋼、低合金鋼部件修復 | STE308-16焊條，STE308-16焊條， （5）藥皮類型：高纖維素鈉型 ‖藥皮主要成分 ： 有機物15%以上，氧化鈦30%左右 ‖焊接電源：直流， ， （8）藥皮類型：石墨型 電源種類：直流或交流 主要特點：藥皮中含有多量石墨，通常用于鑄鐵或堆焊焊條。采用低碳鋼焊芯時，焊接工藝性能較差，飛濺較多，煙霧較大，熔渣少，適于平焊。采用有色金屬焊芯時，能改善其工藝性能，但電流不易過大。， ， ， (1)容易引弧，保證電弧穩定，在焊接過程中飛濺小。， ， ， 高合金鋼以及鋁、銅、鑄鐵等其他金屬材料，其焊芯成分除要求與被焊金屬相近外，同樣也要控制雜質的含量，并按工藝要求常加入某些特定的合金元素。http://www.wanhonghanjie.com， ， ， ， ， 2。(e)一個字母，焊條種類。， ， | 管狀焊絲 | 硬度 | 化學成分（重量%） | 典型用途 | | Tungsmooth 60 | A-91 | 60%碳化鎢、其余為鋼管、A-91中的91為碳化鎢顆粒硬度 | 風機攪拌機葉片、采礦、建筑易損件 |
| 管狀焊絲 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | Mo | Mn | Fe | Ni | Al | 其他 | | Delcrome 11-o | 50 | 3.20 | 14.50 | 0.90 | 0.45 | 1.40 | Bal | | | | 破碎機錘頭、挖土機齒 | | Delcrome 94-o | 57 | 3.20 | 24.50 | 0.70 | | 0.80 | Bal | 2.80 | | | 筑路機零件、攪拌葉片 | | Delcrome 100-o | 57 | 3.80 | 26.50 | 1.40 | 1.30 | 1.90 | Bal | | | | 磨煤輥 | | Delcrome 100HC-o | 60 | 5.50 | 26.50 | 2.40 | 1.30 | 1.90 | Bal | | | | 磨煤輥、破碎輥 | | Delcrome 117-o | 43 | 2.30 | 10.50 | 1.30 | 1.50 | 1.50 | Bal | zr:0.40 | | Cu:0.40 | 破碎輥、錘頭 | | Delcrome 150-o | 58 | 2.20 | 7.00 | | 2.00 | 1.00 | Bal | V:0.20 | | Ti:7.00 | 水泥擠壓輥、錘頭、農具 | | Delcrome 945-o | 57 | 5.00 | 21.50 | 0.70 | 4.50 | 0.70 | Bal | W:2.00 | | Nb:7.00 | 高爐加料槽板、閘閥 | | Build up | 35 | 0.15 | 0.90 | 0.90 | 0.40 | 1.80 | Bal | | | | 碳鋼、低合金鋼恢復尺寸如齒輪、錘頭 | | Ni-Mang-o | 冷硬 | 0.85 | 3.00 | 0.50 | | 14.00 | Bal | 3.00 | | | 破碎機輥、顎板、挖泥機刀片 | | Sta-Mang-o | 冷硬 | 0.10 | 10.00 | 0.50 | 0.80 | 15.50 | Bal | 0.85 | | | 破碎機、鐵鏟、鐵路道岔 | | Multipass 4-o | 34 | 0.15 | 0.70 | 1.10 | 0.30 | 2.00 | Bal | | | | 碳鋼、低合金鋼部件修復 | | Multipass 5-o | 44 | 0.10 | 2.30 | 0.30 | 0.50 | 1.40 | Bal | | | | 拖拉機惰輪、起重機輪 | | Multipass 1265-g | 55 | 0.65 | 5.50 | 0.50 | 1.50 | 1.00 | Bal | W:1.50 | | V:0.30 | 冷沖壓模 | | Delcrome 90G | 48 | 2.40 | 24.00 | 0.60 | | 0.90 | Bal | | | | 鏟斗齒、排氣葉、提升斗 | | Delcrome 94G | 52 | 3.00 | 28.00 | 1.40 | | 1.20 | Bal | B:0.80 | | | 鏟斗齒、攪拌機、破碎輥 | | Mulitpass 106 | | 0.10 | | 0.90 | 5.20 | 1.40 | Bal | 5.20 | | | 管模，鋁軋輥等 | | Delcrome 165 | 62 | 6.80 | 30.00 | 3.00 | 0.50 | 0.50 | Bal | W:4.20 | | Nb:2.60 | 磨煤 輥等耐中等沖擊，強磨粒磨損場合 | | Delstain 414N-o | 47 | 0.20 | 14.00 | 0.50 | 1.00 | 1.30 | Bal | 4.20 | | N:0.22 | 連鑄輥等耐磨耐高溫場合 | | Delstain 431 | 33 | 0.40 | 17.50 | 0.50 | | 1.20 | Bal | | | | 連鑄輥等耐磨耐高溫場合 | | Delcrome 103HD | 60 | 5.60 | 30.00 | 1.10 | 0.80 | 1.20 | Bal | | | Cu:0.10 | 磨煤輥等 | | Stellarc 420 | 430（HV） | 0.3 | 13 | 1 | | 1 | Bal | | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 430 | 400（HV） | 0.7 | 17 | 1 | 0.5 | 1 | Bal | | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 316 | 240（HV） | 0.08 | 18 | 0.7 | 2.5 | 1 | Bal | 13 | | | 具有一定的耐大氣腐蝕及良好的耐磨性，可用于一般機械零件的修復、保護 | | Stellarc 100 | 660（HV） | 5 | 28 | 0.5 | | 1 | Bal | | | | 具有優良的耐磨性 | | Stellarc 250 | | | 1 | 0.5 | 0.5 | 1 | Bal | | | WC:50 | 風機、風管、煙道內壁 | | Stellarc 45 | 400（HV） | | 45 | | | | | Bal | | | 風機、風管、煙道內壁 | | Stellarc 95 | 480（HV） | | | | | | | Bal | 5 | | 打底涂層 | | Stellarc 625 | 260（HV） | 0.08 | 21 | | 9 | | 5 | Bal | 5 | Nb+Ta:4 | 優異的抗高溫腐蝕及耐磨介質 | | Stellarc 276 | | 0.08 | 16 | | 16 | | 5 | Bal | | W:4 | 耐腐蝕性能優異，能抗硫酸、鹽酸或其他有機酸的腐蝕 | STE308-16焊條，STE308-16焊條， ， ， （9）藥皮類型：鐵粉低氫型 ‖藥皮主要成分 ：鈣、鎂的碳酸鹽、螢石和鐵粉 ‖焊接電源：直流或交流， ， ， ， ， 編輯， （8）藥皮類型：低氫鉀型 ‖藥皮主要成分 ： 鈣、鎂的碳酸鹽和螢石 ‖焊接電源： 直流或交流， ， ， 3)硅(si )硅也是一種較好的合金劑，在鋼中加入適量的硅能提高鋼的屈服強度、彈性及抗酸性能；若含量過高，則降低塑性和韌性。在焊接過程中，硅也具有較好的脫氧能力，與氧形成二氧化硅，但它會提高渣的粘度，易促進非金屬夾雜物生成。， (1)容易引弧，保證電弧穩定，在焊接過程中飛濺小。， ， ， | 電焊條 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | B | Cu | 其他 | | Stellite 1 | 48 | 2.20 | 29.00 | 2.00 | 14.00 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 閥座、軸承、刀口等 | | Stellite 6 | 40 | 1.00 | 29.00 | 1.00 | 4.50 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 發動機氣門、高溫高壓閥門、渦輪機葉片 | | Stellite 12 | 44 | 1.30 | 29.00 | 1.00 | 9.00 | 3.00 | 0.50 | 3.00 | Bal | 1.00 | | | | 高溫高壓閥門、鋸齒、螺旋推桿等 | | Stellite 21 | 23 | 0.30 | 28.00 | 1.00 | | 2.50 | 5.50 | 2.50 | Bal | 2.00 | | | | 渦輪機葉片、閥座、熱沖模 | | Stellite 25 | 冷硬 | 0.15 | 20.00 | 1.00 | 14.00 | 3.00 | 0.50 | 10.00 | Bal | 1.50 | | | | 高溫耐蝕密封面、擠壓模 | | Nistelle C | | 0.10 | 17.00 | | 5.00 | 6.00 | 17.00 | Bal | | | | | | 高溫耐蝕密封環 | | Ni-Mang | 冷硬 | 0.60 | 2.70 | 0.20 | | Bal | | 3.70 | | 13.50 | | | | 錘式破碎機、高錳鋼部件焊接 | | STE 308-16 | | 0.08 | 19.50 | 0.90 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | | 用于焊接Cr18Ni8不銹鋼 | | STE 308L-16 | | 0.03 | 19.50 | 0.90 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | | 用于焊接超低碳Cr18Ni8不銹鋼 | | STE 309-16 | | 0.15 | 23.50 | 0.90 | | Bal | 0.50 | 13.00 | | 0.80 | | 0.50 | | 用于焊接Cr22Nil2不銹鋼及用于不銹鋼與低碳鋼或低合金鋼之間的焊接 | | STE 309L-16 | | 0.02 | 23.50 | 0.90 | | Bal | 0.50 | 13.00 | | 0.80 | | 0.50 | | 打底層焊接，異種鋼焊接，易產生裂紋部位的焊接 | | STE 309Mo-16 | | 0.12 | 23.50 | 0.90 | | Bal | 2.50 | 13.00 | | 0.80 | | | | 用于焊接Cr22Nil2-Mo不銹鋼 | | STE 309MoL-16 | | 0.03 | 23.50 | 0.90 | | Bal | 2.50 | 13.00 | | 0.80 | | | | 用于焊接超低碳Cr22Nil2Mo不銹鋼 | | STE 310-16 | | 0.20 | 26.50 | 0.75 | | Bal | 0.50 | 21.50 | | 1.50 | | 0.50 | | 用于焊接Cr25Ni20不銹鋼 | | STE 310Mo-16 | | 0.08 | 26.50 | 0.75 | | Bal | 2.50 | 21.00 | | 1.20 | | 0.50 | | 耐硫酸腐蝕、抗裂性、高溫性能優良 | | STE 316-16 | | 0.05 | 18.50 | 0.90 | | Bal | 2.50 | 12.50 | | 0.80 | | 0.50 | | 用于焊接Cr18Ni12Mo2不銹鋼 | | STE 316L-16 | | 0.03 | 18.50 | 0.90 | | Bal | 2.50 | 12.50 | | 0.80 | | 0.50 | | 用于焊接超低碳Cr18Ni12Mo2不銹鋼 | | STE 316LF | | 0.02 | 18.00 | 0.75 | | Bal | 2.70 | 16.00 | | 2.00 | | 0.50 | | 耐尿素腐蝕性優良 | | STE 347-16 | | 0.08 | 19.50 | 0.50 | | Bal | 0.50 | 10.00 | | 0.80 | | 0.50 | 8xc-1.00 | 用于焊接Cr18Ni8含鈮或鈦的不銹鋼 | | STE 997 | 56 | 0.60 | 5.50 | 0.80 | | Bal | 4.00 | W:7.0 | | 0.70 | | | | 低氫型高速鋼焊條 | | D 287 | 40 | 0.10 | 14.00 | 0.50 | | Bal | 1.00 | 5.00 | | 0.50 | | | | 水泵、水輪機部件 | | D 907 | 冷硬 | 0.20 | 21.00 | 1.00 | 2.50 | Bal | 3.00 | | 20.00 | 1.50 | | | | 熱剪刀片 | | Delcrome 90sc | 52 | 2.10 | 26.00 | 1.10 | | Bal | | | | 0.90 | | | | 挖掘設備、破碎輥、錘 | | Delcrome 91 | 55 | 3.00 | 31.00 | 0.60 | | Bal | 1.30 | | | 0.90 | | | | 破碎機輥、錘頭、泥漿泵部件 | | Delcrome 94 | 53 | 3.00 | 31.00 | 0.40 | | Bal | 1.30 | | | 0.90 | | | | 鏟斗齒、攪拌機、挖掘采礦設備 | | Delcrome 945 | 58 | 5.40 | 1.20 | | Bal | | | | 1.00 | | | Nb:5.00 | 耐侵蝕、抗高溫腐蝕及磨損場合 | | Delcrome 23 | 44 | 0.20 | 5.50 | 1.00 | &n, bsp;&, amp;, lt;, /TD> | Bal | 2.50 | V:7.0 | | 1.20 | | | | 低氫型焊條，用于鍛模、沖模 | STE308-16焊條，STE308-16焊條， ， （2）藥皮類型：氧化鈦型 電源種類：直流或交流 主要特點：含多量氧化鈦，焊條工藝性能良好，電弧穩定，再引弧方便，飛濺很小，熔深較淺，熔渣覆蓋性良好，脫渣容易，焊縫波紋特別美觀，可全位置焊接，尤宜于薄板焊接，但焊縫塑性和抗裂性稍差。隨藥皮中鉀、鈉及鐵粉等用量的變化，分為高鈦鉀型、高鈦鈉型及鐵粉鈦型等， (5)適應各種位置的焊接。， ， ， 焊條焊接時，焊芯金屬占整個焊縫金屬的一部分。所以焊芯的化學成分，直接影響焊縫的質量。因此，作為焊條芯用的鋼絲都單獨規定了它的牌號與成分。如果用于埋弧自動焊、電渣焊、氣體保護焊、氣焊等熔焊方法作填充金屬時，則稱為焊絲。http://www.wanhonghanjie.com， ， 焊條(coveredelectrode)，是在金屬焊芯外將涂料(藥皮)均勻、向心地壓涂在焊芯上。焊芯即焊條的金屬芯，為了保證焊縫的質量與性能，對焊芯中各金屬元素的含量都有嚴格的規定，特別是對有害雜質（如硫、磷等)的含量，應有嚴格的限制，優于母材。焊條由焊芯及藥皮兩部分構成。其種類不同，焊芯也不同。焊芯成分直接影響著焊縫金屬的成分和性能，所以焊芯中的有害元素要盡量少。http://www.wanhonghanjie.com， （2）藥皮類型：氧化鈦型 電源種類：直流或交流 主要特點：含多量氧化鈦，焊條工藝性能良好，電弧穩定，再引弧方便，飛濺很小，熔深較淺，熔渣覆蓋性良好，脫渣容易，焊縫波紋特別美觀，可全位置焊接，尤宜于薄板焊接，但焊縫塑性和抗裂性稍差。隨藥皮中鉀、鈉及鐵粉等用量的變化，分為高鈦鉀型、高鈦鈉型及鐵粉鈦型等， ， ， (3)熔渣的比重應小于熔化金屬的比重，凝固溫度也應稍低于金屬凝固溫度，渣殼應易脫掉；， （船用焊條除外）， ， 焊芯是根據國家標準“焊接用鋼絲”（gb 1300-77)的規定分類的，用于焊接的專用鋼絲可分為碳素結構鋼、合金結構鋼、不銹鋼三類。， | 電焊條 | 硬度 | 化學成分（重量%） | 典型用途 | | Electrode | A-91 | 60%碳化鎢、其余為鋼管、A-91中的91為碳化鎢顆粒硬度 | 風機攪拌機葉片、采礦、建筑易損件 | | 鑄棒 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | | Stellite 1 | 53 | 2.50 | 29.50 | 1.20 | 12.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 閥座、軸承、刀口等 | | Stellite 3 | 54 | 2.40 | 31.00 | 1.00 | 12.50 | 3.00 | | 3.00 | Bal | 1.00 | 針閥座、閥座、軋鋼導向輥 | | Stellite 4 | 48 | 0.90 | 32.00 | 1.00 | 13.50 | 1.00 | 0.50 | 0.50 | Bal | 0.50 | 熱壓模、熱擠壓模、干電池工業 | | Stellite 6 | 43 | 1.20 | 29.00 | 1.20 | 4.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 發動機氣門、高溫高壓閥門、渦輪機葉片 | | Stellite 12 | 47 | 1.45 | 29.00 | 2.00 | 8.50 | 3.00 | 1.00 | 3.00 | Bal | 1.00 | 高溫高壓閥門、鋸齒、螺旋推桿等 | | Stellite 20 | 54 | 2.45 | 32.50 | 1.00 | 17.00 | 3.00 | 1.00 | 3.00 | Bal | 0.50 | 軸承套筒、耐磨板 | | Stellite 21 | 20 | 0.25 | 27.00 | 1.00 | 0.15 | 2.00 | 5.50 | 2.50 | Bal | 1.00 | 渦輪機葉片、各種液體閥、閥座、熱沖模等 | | Stellite 31 | 33 | 0.50 | 25.50 | 1.00 | 7.50 | 2.00 | 1.00 | 10.50 | Bal | 1.00 | 燃氣渦輪葉片 | | Stellite 190 | 58 | 3.20 | 26.00 | 1.00 | 14.00 | 5.00 | 1.00 | 3.00 | Bal | 1.00 | 石油鉆具 | | Stellite 706 | 42 | 1.20 | 30.00 | 1.20 | | 2.00 | 5.00 | 2.00 | Bal | 1.00 | 發動機氣門、高溫高壓閥門 | | Stellite 712 | 50 | 2.00 | 29.00 | 2.00 | | 2.00 | 8.50 | 2.00 | Bal | 2.00 | 高溫高壓閥門、螺旋推桿 | | Tribaloy 400 | 53 | 0.08 | 8.50 | 2.60 | | 1.50 | 28.50 | 1.50 | Bal | | 用于高溫強腐介質中的閘閥、擠塑器 | | Tribaloy 800 | 55 | 0.08 | 18.00 | 3.40 | | 1.50 | 28.50 | 1.50 | Bal | | 用于高溫強腐介質中的閘閥、擠塑器 | | Stellite F | 40 | 1.75 | 25.50 | 1.10 | | 1.15 | 0.60 | 22.50 | Bal | 0.30 | 內燃機進排氣閥 | STE308-16焊條，STE308-16焊條， ， （5）藥皮類型：氧化鐵型 電源種類： 直流或交流 主要特點：藥皮中含多量氧化鐵和較多的錳鐵脫氧劑，熔深大，熔化速度快，焊接生產率較高，電弧穩定，再引弧方便，立焊、仰焊較困難，飛濺稍大，焊縫抗熱裂性能較好，適用于中厚板焊接。由于電弧吹力大，適于野外操作。若藥皮中加入一定量的鐵粉，為鐵粉氧化鈦型。， 焊條牌號的編制方法 ， http://www.wanhonghanjie.com， （7）藥皮類型：低氫鉀型 （低氫鈉型） 電源種類：直流或交流 （直流） 主要特點：藥皮成分以碳酸鹽和螢石為主。焊條使用前須經300～400℃烘焙。短弧操作，焊接工藝性一般，可全位置焊接。焊縫有良好的抗裂性和綜合力學性力。適于焊接重要的焊接結構。按照藥皮中穩弧劑量、鐵粉量和黏結劑不同，分為低氫鈉型、低氫鉀型和鐵粉低氫型等http://www.wanhonghanjie.com， ， ， ， ， （3）藥皮類型：鈦鈣型 電源種類： 直流或交流 主要特點：藥皮中含氧化鈦30%以上，鈣、鎂的碳酸鹽20%以下，焊條工藝性能良好，熔渣流動性好，熔深一般，電弧穩定，焊縫美觀，脫渣方便，適用于全位置焊接，如j422即屬此類型，是目前碳鋼焊條中使用最廣泛的一種焊條。， 以結構鋼為例：牌號,編制法。結xxx,結為結構鋼焊條,第3個數字,代表藥皮類型,焊接電流要求,第1、2數:代表焊縫金屬抗拉強度 。， ， ， 六、藥皮在焊接過程中起著極為重要的作用。若采用無藥皮的光焊條焊接，則在焊接過程中，空氣中的氧和氮會大量侵入熔化金屬，將金屬鐵和有益元素碳、硅、錳等氧化和氮化形成各種氧化物和氮化物，并殘留在焊縫中，造成焊縫夾渣或裂紋。而熔入熔池中的氣體可能使焊縫產生大量氣孔，這些因素都能使焊縫的機械性能（強度、沖擊值等）大大降低，同時使焊縫變脆。此外采用光焊條焊接，電弧很不穩定，飛濺嚴重，焊縫成形很差。， ，
| 鑄棒 | 硬度 | 化學成分（重量%） | 典型用途 | | C | Cr | Si | W | Fe | Mo | Ni | Co | Mn | B | | Deloro 40 | 40 | 0.30 | 7.50 | 3.50 | | 2.20 | 0.10 | Bal | | 0.10 | 1.70 | 螺旋送料器、模芯、核工業中閥門的密封面 | | Deloro 45 | 45 | 0.37 | 8.75 | 3.80 | | 4.00 | 0.10 | Bal | | 0.10 | 2.00 | 排氣閥密封面、柱塞 | | Deloro 50 | 50 | 0.45 | 11.25 | 4.00 | | 2.80 | 0.10 | Bal | | 0.10 | 2.20 | 泵軸、紙漿刀、閥門、密封環、軸套 | | Deloro 55 | 55 | 0.50 | 11.00 | 3.60 | | 4.50 | 0.10 | Bal | | 0.50 | 2.10 | 閥門、密封環、軸套 | | Deloro 60 | 59 | 0.65 | 15.00 | 4.30 | | 4.00 | 0.10 | Bal | | 0.10 | 3.10 | 擠壓模、螺旋筒體、泵葉、柱塞 | | Deloro 6325 | 56 | 0.50 | 16.00 | 4.00 | | 4.50 | 3.00 | Bal | | 0.10 | 3.50 | 耐蝕泵、軸、軸套 | | Tribaloy 700 | 54 | 0.08 | 15.50 | 3.40 | | 1.50 | 32.50 | Bal | 1.50 | | | 核工業應用抗蝕抗氧化抗輻射 | | Nistelle B | 冷硬 | 0.10 | 1.00 | 1.00 | | 5.00 | 28.00 | Bal | 2.50 | 1.00 | | 高溫耐蝕密封環 | STE308-16焊條， 1)碳(c)碳是鋼中的主要合金元素，當含碳量增加時，鋼的強度、硬度明顯提高，而塑性降低。在焊接過程中，碳起到一定的脫氧作用，在電弧高溫作用下與氧發生化合作用，生成一氧化碳和二氧化碳氣體，將電弧區和熔池周圍空氣排除，防止空氣中的氧、氮有害氣體對熔池產生的不良影響，減少焊縫金屬中氧和氮的含量。若含碳量過高，還原作用劇烈，會引起較大的飛濺和氣孔。考慮到碳對鋼的淬硬性及其對裂紋敏感性增加的影響，低碳鋼焊芯的含碳量一般為0. 1%。， ， 1。(chh) 二個字母，中國航海產品代號。， ， 焊芯是根據國家標準“焊接用鋼絲”（gb 1300-77)的規定分類的，用于焊接的專用鋼絲可分為碳素結構鋼、合金結構鋼、不銹鋼三類。， ， 5)鎳(ni）鎳對鋼的韌性有比較顯著的效果，一般低溫沖擊值要求較高時，適當摻入一些鎳。， 六、藥皮在焊接過程中起著極為重要的作用。若采用無藥皮的光焊條焊接，則在焊接過程中，空氣中的氧和氮會大量侵入熔化金屬，將金屬鐵和有益元素碳、硅、錳等氧化和氮化形成各種氧化物和氮化物，并殘留在焊縫中，造成焊縫夾渣或裂紋。而熔入熔池中的氣體可能使焊縫產生大量氣孔，這些因素都能使焊縫的機械性能（強度、沖擊值等）大大降低，同時使焊縫變脆。此外采用光焊條焊接，電弧很不穩定，飛濺嚴重，焊縫成形很差。， （9）藥皮類型：鹽基型 電源種類：直流 主要特點： 藥皮中含多量氯化物和氟化物，主要用于鋁及鋁合金焊條。吸潮性強，焊前要烘干。藥皮熔點低，熔化速度快。采用直流電源，焊接工藝性較差，短弧操作，熔渣有腐蝕性，焊后需用熱水清洗。， ， 1)碳(c)碳是鋼中的主要合金元素，當含碳量增加時，鋼的強度、硬度明顯提高，而塑性降低。在焊接過程中，碳起到一定的脫氧作用，在電弧高溫作用下與氧發生化合作用，生成一氧化碳和二氧化碳氣體，將電弧區和熔池周圍空氣排除，防止空氣中的氧、氮有害氣體對熔池產生的不良影響，減少焊縫金屬中氧和氮的含量。若含碳量過高，還原作用劇烈，會引起較大的飛濺和氣孔。考慮到碳對鋼的淬硬性及其對裂紋敏感性增加的影響，低碳鋼焊芯的含碳量一般為0. 1%。， 編輯， （8）藥皮類型：低氫鉀型 ‖藥皮主要成分 ： 鈣、鎂的碳酸鹽和螢石 ‖焊接電源： 直流或交流， ， ， 焊接碳鋼及低合金鋼的焊芯， 一般都選用低碳鋼作為焊芯，并添加錳、硅、鉻、鎳等成分(詳見焊絲國家標準gb1300一77)。采用低碳的原因一方面是含碳量低時鋼絲塑性好，焊絲拉拔比較容易，另一方面可降低還原性氣體co含量，減少飛濺或氣孔，并可增高焊縫金屬凝固時的溫度，對仰焊有利。加入其他合金元素主要為保證焊縫的綜合機械性能，同時對焊接工藝性能及去除雜質，也有一定作用。， 三、保證焊縫脫氧、去硫磷雜質。焊接過程中雖然進行了保護，但仍難免有少量氧進入熔池，使金屬及合金元素氧化，燒損合金元素，降低焊縫質量。因此，需要在焊條藥皮中加入還原劑(如錳、硅、鈦、鋁等)，使已進入熔池的氧化物還原。http://www.wanhonghanjie.com， (5)適應各種位置的焊接。， 七、焊條藥皮類型及主要特點。按照藥皮的主要成分可以確定焊條的藥皮類型。由于藥皮配方組成不同，致使各種藥皮類型焊條的熔渣特性、焊接工藝性能以及焊縫金屬力學性能有很大差別。即使是同一類型藥皮，但不同牌號的焊條也因為藥皮成分和配比不同，焊條的工藝性能等也會出現明顯的差別。， ， （3）藥皮類型：鈦鐵礦型 ‖藥皮主要成分 ：鈦鐵礦≥30% ‖焊接電源：直流或交流， ， ， 1)碳(c)碳是鋼中的主要合金元素，當含碳量增加時，鋼的強度、硬度明顯提高，而塑性降低。在焊接過程中，碳起到一定的脫氧作用，在電弧高溫作用下與氧發生化合作用，生成一氧化碳和二氧化碳氣體，將電弧區和熔池周圍空氣排除，防止空氣中的氧、氮有害氣體對熔池產生的不良影響，減少焊縫金屬中氧和氮的含量。若含碳量過高，還原作用劇烈，會引起較大的飛濺和氣孔。考慮到碳對鋼的淬硬性及其對裂紋敏感性增加的影響，低碳鋼焊芯的含碳量一般為0. 1%。， （7）藥皮類型：低氫鉀型 （低氫鈉型） 電源種類：直流或交流 （直流） 主要特點：藥皮成分以碳酸鹽和螢石為主。焊條使用前須經300～400℃烘焙。短弧操作，焊接工藝性一般，可全位置焊接。焊縫有良好的抗裂性和綜合力學性力。適于焊接重要的焊接結構。按照藥皮中穩弧劑量、鐵粉量和黏結劑不同，分為低氫鈉型、低氫鉀型和鐵粉低氫型等http://www.wanhonghanjie.com， | 
