邢臺飛機牌15%銀焊條市場價
(2)藥皮熔化速度應慢于焊芯熔化速度，以造成喇叭狀的套簡(套筒長度應小于焊芯直徑），有利于熔滴過渡和造成保護氣氛；
| Category | Trade-mark | Specification | Melting | Chemical | Application | Equivalent |
| Copper 銅鋅 | L103 | Wire & rod | 885-888 | Cu54 Zn Rem. | Brazing of copper, bronze and steel, subjected to low load. | 邢臺飛機牌15%銀焊條市場價 |
| L104 | Foil | 890-930 | Cu57 Mn2 | Brazing of carbide cutting tool. | ||
| Copper 銅磷 | L201 | Cast rod, wire & rod, powder | 710-800 | P7 Cu Rem. | Brazing of copper and copper alloys. | BCuP-2 |
| L204 | Cast rod, wire | 640-815 | P5 Ag15 | Brazing of copper, copper alloys, silver and molybdenum etc. | BCuP-5 | |
| L205 | Cast rod, wire & rod, powder | 640-800 | P6 Ag5 | Brazing of copper and copper alloys. | BCuP-3 | |
| L207 | Cast rod, wire & rod | 640-770 | P7 Ag5 | Brazing of copper and copper alloys. | BCuP-7 | |
| L209 | Cast rod, wire | 684-710 | P7 Ag2 | Brazing of copper and copper alloys. | BCuP-6 | |
| Silver 銀基 | L302 | Wire & rod | 745-775 | Ag25 Cu40 | Brazing of copper, copper alloys, steel and stainless steel etc. | 三、保證焊縫脫氧、去硫磷雜質。焊接過程中雖然進行了保護，但仍難免有少量氧進入熔池，使金屬及合金元素氧化，燒損合金元素，降低焊縫質量。因此，需要在焊條藥皮中加入還原劑(如錳、硅、鈦、鋁等)，使已進入熔池的氧化物還原。 |
| L303 | Wire & rod | 660-725 | Ag45 Cu30 | Brazing of copper, copper alloys, steel and stainless steel etc. | BAg-5 | |
| L303F | Flux coated rod | 660-725 | Ag45 Cu30 | L303 coated with flux, the same application as L303. | BAg-5 | |
| L304 | Foil | 690-775 | Ag50 Cu34 | Brazing of copper, copper alloys and steel etc. | BAg-6 | |
| L308 | Wire & rod | 779-780 | Ag72 Cu Rem. | Brazing of copper and nickel under vacuum or reducing protective atmosphere. | BAg-8 | |
| L312 | Wire & rod | 595-605 |
| Brazing of copper, copper alloys, steel and stainless steel etc. | 焊條藥皮類型分類 | |
| L313 | Wire & rod | 625-635 |
| Brazing of copper, copper alloys, steel and stainless steel etc. | BAg-1a | |
| L321 | Wire & rod 絲 | 615-650 |
| Brazing of copper, copper alloys, steel and stainless steel etc. | BAg-7 | |
| L323 | Wire & rod | 665-755 |
| Brazing of copper, copper alloys, steel and stainless steel etc. | 焊條就是涂有藥皮的供焊條電弧焊使用的熔化電極，它是由藥皮和焊芯兩部分組成的。在焊條前端藥皮有45°左右的倒角，這是為了便于引弧。在尾部有一段裸焊芯，約占焊條總長1/16，便于焊鉗夾持并有利于導電。焊條的直徑實際上是指焊芯直徑）通常為2、2.5、3.2或3、4、5或6mm等幾種規格，最常用的是小3.2、小4、小5三種，其長度“L”一般在200～550 mm之間。 | |
| L325 | Wire & rod | 645-685 |
| Brazing of copper, copper alloys, steel and stainless steel etc. | BAg-36 | |
| L326 | Wire & rod | 650-720 |
| Brazing of copper, copper alloys, steel and stainless steel etc. | BAg-34 | |
| Aluminum base 鋁基 | L400 | Cast rod, wire & rod | 577-582 | Si11.5 | Brazing of aluminum and aluminum alloys. | BAlSi-4 |
| L401 | Cast rod | 525-535 | Si5 Cu28 | Brazing of aluminum and aluminum alloys. | 編輯 | |
| Tin lead 錫鉛 | L600 | Wire & rod | 183-185 | Sn60 Sb≤0.8 | Soldering of fusible metals and heat-treated part. | 60Sn |
| L601 | Wire & rod | 183-227 | Sn18 Sb2 | Soldering of copper, copper alloys and galvanized iron plain sheet. | 18Sn | |
| L602 | Wire & rod | 183-256 | Sn30 Sb2 | Soldering of copper, brass, copper alloys and galvanized iron plain sheet. | 30Sn | |
| L603 | Wire & rod | 183-235 | Sn40 Sb2 | Soldering of copper, copper alloys, steel and zinc parts. | 40Sn | |
| L604 | Wire & rod | 183-222 | Sn90 Sb≤0.15 | Soldering of copper and steel for food and medicine field. | 90Sn | |
| L605 | Wire & rod | 232-240 | Ag5 Sn95 | Soldering of copper and steel for electrical and food field. | ||
| L608 | Wire & rod | 295-305 | Sn5.5 Ag2.5 | Soldering of copper, copper alloys, steel and stainless steel. | 高合金鋼以及鋁、銅、鑄鐵等其他金屬材料，其焊芯成分除要求與被焊金屬相近外，同樣也要控制雜質的含量，并按工藝要求常加入某些特定的合金元素。 | |
| Nickel base 鎳基 | L702 | Powder | 970-1000 | Cr7 B3 Si4 | Brazing of stainless steel under vacuum or protective atmosphere. | BNi-2 |
邢臺飛機牌15%銀焊條市場價
(3)熔渣的比重應小于熔化金屬的比重，凝固溫度也應稍低于金屬凝固溫度，渣殼應易脫掉；